选取TA2纯钛为研究对象，在箱式电阻炉中进行不同温度与不同时间的热氧化处理，研究了不同工艺热氧化处理试样在36％～38％HCl（室温）和30％H2O2（36.5℃）中的耐腐蚀性。采用扫描电子显微镜（SEM）观察了热氧化处理试样表面形貌， XRD进行了物相分析，用电子天平称重。研究结果表明， TA2纯钛在600℃以上热氧化处理在其表面形成了比原始态更厚的金红石型TiO2氧化膜，且TiO2氧化膜随热氧化温度升高而加厚；热氧化后TA2试样在36％～38％HCl和30％H2 O2中耐腐蚀性明显改善，改善TA2耐蚀性的最佳热氧化工艺条件为：热氧化温度700℃；热氧化时间330～500 min。
Commercially pure titanium ( CP-Ti) TA2 samples were subjected to thermal oxidation ( TO) treatment at different temperature .The morphological feature , structural characteristics and weight of thermally oxidized samples were studied by scanning electron microscope (SEM), X-ray diffraction(XRD) and electronic balance.The corrosion resistance of thermally oxidized samples in 36%~38% HCl ( room temperature ) and 30% H2 O2 ( 36.5 ℃) were investigated .The results show that , when the TO temperature is above 600 ℃, the oxidized layer is composed of TiO2 , and the thickness of TiO 2 oxidized layer increases with the temperature increased .And the corrosion resistance in HCl and H 2 O2 increases significantly after TO treatment , and the optimum TO condition is treating temperature of 700 ℃and duration of 330~500 min.
参考文献
| [1] | Boyer R R .An overview on the use of titanium in the aero-space industry[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1996,213(1/2):103-114. |
| [2] | Rack HJ;Qazi JI .Titanium alloys for biomedical applications[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2006(8):1269-1277. |
| [3] | Gorynin, IV .Titanium alloys for marine application[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(2):112-116. |
| [4] | He LJ;Zhang XN;Tong CD .Surface modification of pure titanium treated with B4C at high temperature[J].Surface & Coatings Technology,2006(9):3016-3020. |
| [5] | Atar E;Kayali ES;Cimenoglu H .Characteristics and wear performance of borided Ti6Al4V alloy[J].Surface & Coatings Technology,2008(19):4583-4590. |
| [6] | Bloyce A.;Dong H.;Bell T.;Qi PY. .Surface modification of titanium alloys for combined improvements in corrosion and wear resistance[J].Surface & Coatings Technology,1998(2/3):125-132. |
| [7] | 朱媛媛,王庆良,玄甲申.钛合金微弧氧化层的摩擦学性能研究[J].润滑与密封,2007(11):118-121. |
| [8] | 严伟,王小祥.热氧化处理钛表面渗氧层的组织与性能研究[J].稀有金属材料与工程,2005(03):471-474. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%