研究铁镍基高温合金GH2984在700~750℃蠕变期间的显微组织演变及其对性能的影响。结果表明：在(700℃，300 MPa)蠕变条件下，合金持久寿命仅160 h，变形过程中晶界处的应力集中并促进裂纹的萌生与扩展是造成合金失效的主要原因。应力降至200 MPa时，晶粒旋转导致晶界处应力集中得到释放，抑制裂纹萌生并进而使合金持久寿命明显增长。然而，随着蠕变温度的增加，晶粒在变形过程中伴随出现动态再结晶。这一现象虽然使得合金持久塑性有所增加，但晶粒加工硬化程度较低造成合金持久寿命明显缩短。
The microstructure evolution and its effect on the properties of GH2984 alloy between 700 and 750℃were investigated. The results show the rupture life is only about 160 h when the alloy was crept at 700℃ and 300 MPa. The stress concentration and consequently crack nucleation and propagation are the main reason for failure of the alloy. When the stress decreases, the stress concentration is released by the grain rotation. It inhibits the crack nucleation and thus extends the alloy rupture life obviously. However, accompanied with the grain deformation proceeding, the dynamic recrystallization occurs when the creep temperature increases. This leads to the increases of the alloy creep ductility, but decreases the alloy rupture life because of the lower work hardening extent.
参考文献
| [1] | Yan, J.;Gu, Y.;Lu, J..On precipitates in Fe-Ni base alloys used for USC boilers[J].Materials Science and Technology: MST: A publication of the Institute of Metals,20154(4):389-399. |
| [2] | R. Viswanathan;K. Coleman;U. Rao.Materials for ultra-supercritical coal-fired power plant boilers[J].International Journal of Pressure Vessels and Piping,200611/12(11/12):778-783. |
| [3] | Y. Yuan;Z.H. Zhong;Z.S. Yu;H.F. Yin;Y.Y. Dang;X.B. Zhao;Z. Yang;J.T. Lu;J.B. Yan;Y. Gu.Microstructural evolution and compressive deformation of a new Ni-Fe base superalloy after long term thermal exposure at 700 °C[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2014:364-369. |
| [4] | 郭建亭;杜秀魁.一种性能优异的过热器管材用高温合金GH2984[J].金属学报,2005(11):1221-1227. |
| [5] | 肖旋;赵海强;王常帅;郭永安;郭建亭;周兰章.B和P对GH984合金组织和力学性能的影响[J].金属学报,2013(4):421-427. |
| [6] | Tingting Wang;Changshuai Wang;Jianting Guo.Stability of Microstructure and Mechanical Properties of GH984G Alloy during Long-term Thermal Exposure[J].Materials Science Forum,2013:647-653. |
| [7] | 郭建亭;袁超;侯介山.高温合金的蠕变及疲劳-蠕变-环境交互作用规律和机理[J].中国有色金属学报,2011(3):487-504. |
| [8] | 侯介山;丛培娟;周兰章;秦学智;袁超;郭建亭.Hf对抗热腐蚀镍基高温合金微观组织和力学性能的影响[J].中国有色金属学报,2011(5):945-953. |
| [9] | 田素贵;谢君;周晓明;钱本江;伦建伟;于丽丽;汪武祥.淬火工艺对FGH95合金组织结构与蠕变性能的影响[J].中国有色金属学报,2010(5):852-858. |
| [10] | ZHIHONG ZHONG;YUEFENG GU;YONG YUAN.Tensile Properties and Deformation Characteristics of a Ni-Fe-Base Superalloy for Steam Boiler Applications[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,20141(1):343-350. |
| [11] | Jian-Min Zhang;Yan Zhang;Ke-Wei Xu.Dependence of stresses and strain energies on grain orientations in FCC metal films[J].Journal of Crystal Growth,20053(3):427-435. |
| [12] | N. Dudova;A. Belyakov;T. Sakai.Dynamic recrystallization mechanisms operating in a Ni-20%Cr alloy under hot-to-warm working[J].Acta materialia,201010(10):3624-3632. |
| [13] | Branger V.;Mathona M.H.."IN-SITU" NEUTRON DIFFRACTION STUDY OF THE CUBE CRYSTALLOGRAPHIC TEXTURE DEVELOPMENT IN Fe53 percent -Ni ALLOY DURING RECRYSTALLIZATION[J].Scripta materialia,20004(4):325-330. |
| [14] | Taku Sakai;Andrey Belyakov;Rustam Kaibyshev;Hiromi Miura;John J. Jonas.Dynamic and post-dynamic recrystallization under hot, cold and severe plastic deformation conditions[J].Progress in materials science,2014Mar.(Mar.):130-207. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%