使用烧结法制备了LZS系微晶玻璃.采用差热分析(DTA)、X射线衍射分析(XRD)、扫描电镜(SEM)等分析手段对该系统微晶玻璃的析晶过程和微观结构进行了研究.通过正交试验讨论了热处理参数对微晶玻璃热膨胀性能的影响.结果表明:随着晶化温度的升高,主晶相由硅酸锂锌转变为石英,晶相含量随之增高;晶体为棒状,随温度升高和时间延长而增大;各参数对热膨胀性影响大小为晶化温度>晶化时间>核化时间>核化温度;可以通过调节热处理工艺参数调节热膨胀系数,热膨胀系数决定于主晶相的热膨胀系数及晶相含量.
参考文献
| [1] | Shelby J E;Nichols M C .Effect of Thermal History on the Properties of a Willemite Glass-ceramics[J].Journal of the American Ceramic Society,1983,66(03):200-204. |
| [2] | Shelby J E .The Effect of Crystal Content on the Properties of Willemite Glass-ceramics[J].Journal of Non-Crystalline Solids,1981,43(02):255-265. |
| [3] | 张永爱,刘浩,袁坚.Li2O-ZnO-SiO2系微晶玻璃结构和性能的研究[J].玻璃,2004(03):3-5,24. |
| [4] | Demirkesen E;Maytalman E .Effect of Al2O3 Additions on the Crystallization Behaviour and Bending Strength of a Li2O-ZnO-SiO2 Glass-ceramic[J].Ceramics International,2001,27:99-104. |
| [5] | Demirkesen E;Go ller G .Effect of Al2O3 Additions on the Acid Durability of a Li2O-ZnO-SiO2 Glass and Its Glass-ceramic[J].Ceramics International,2003,29:463-469. |
| [6] | Madhumita Goswami;P. Sengupta;Kuldeep Sharma .Crystallization behaviour of Li_2O-ZnO-SiO_2 glass-ceramics system[J].Ceramics International,2007(5):863-867. |
| [7] | 郑少华;姜奉华.试验设计与数据处理[M].北京:中国建筑工业出版社,2004:67. |
| [8] | 麦克米伦 P W;王仞千.微晶玻璃[M].北京:中国建筑工业出版社,1988:247. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%