利用质子交换膜燃料电池用过的废旧碳纸,采用球磨法制备了石墨纳米纤维(GNF, BET比表面积为229.3 m2/g), 并以GNF作为载体制备了Pt/GNF催化剂(电化学比表面积为98 m2/g). 与传统的以Vulcan XC-72碳黑为载体的Pt/XC-72催化剂相比,其电化学比表面积及Pt粒径大小相近. 采用恒电位氧化法考察了GNF, XC-72, Pt/GNF和Pt/XC-72的电化学稳定性. 结果表明,在相同条件下, XC-72的峰电流增加了60%, 而GNF增加了2%; Pt/XC-72的腐蚀电流比Pt/GNF的大40%; 恒电位氧化 60 h 后, Pt/XC-72约有84.7%的电化学比表面积损失, Pt/GNF仅损失37.2%. 这表明GNF的抗腐蚀性优于XC-72, 有希望成为质子交换膜燃料电池抗腐蚀的催化剂载体.
参考文献
| [1] | Liu D;Case S .[J].Journal of Power Sources,2006,162(01):521. |
| [2] | Liu H S;Song Ch J;Zhang L;Zhang J J Wang H J Wilkinson D P .[J].Journal of Power Sources,2006,155(02):95. |
| [3] | Tang H;Qi Zh H;Ramani M;Elter J F .[J].Journal of Power Sources,2006,158(02):1306. |
| [4] | Cai M;Ruthkosky M S;Merzougui B;Swathirajan S Balogh M P Oh S H .[J].Journal of Power Sources,2006,160(02):977. |
| [5] | Borup R L;Davey J R;Garzon F H;Wood D L Inbody M A .[J].Journal of Power Sources,2006,163(01):76. |
| [6] | Wang X;Li W Zh;Chen Zh W;Waje M Yan Y Sh .[J].Journal of Power Sources,2006,158(01):154. |
| [7] | Shao Y Y;Yin G P;Zhang J;Gao Y Zh .[J].Electrochimica Acta,2006,51(26):5853. |
| [8] | Nie M;Shen P K;Wu M;Wei Z D Meng H .[J].Journal of Power Sources,2006,162(01):173. |
| [9] | 徐洪峰,林治银,邱艳玲,唐倩.用于质子交换膜燃料电池的碳载铂电催化剂[J].催化学报,2003(02):143-148. |
| [10] | Burchell T D;Judkins R R .[J].Energy Conversion and Management,1997,38:S99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%