研究了聚酯纤维和碳纤维磷铝酸盐水泥(以下简称PALC)混凝土的力学性能.结果表明,在90 d龄期时,聚酯纤维和碳纤维磷铝酸盐水泥混凝土的抗压强度分别达到了59.5 MPa、53.7 MPa,比同龄期素混凝土试样的45.7 MPa分别提高了30.6%和17.5%;而劈拉强度分别达到了5.85 MPa和5.02 MPa,比同龄期素混凝土试样的4.15 MPa分别提高了41.0%和21.0%,聚酯纤维混凝土的劈拉强度、抗压强度都明显高于碳纤维混凝土,而且碳纤维和聚酯纤维对磷铝酸盐水泥混凝土均有明显的约束其裂缝扩展的能力,表现为在28 d龄期时,碳纤维混凝土的断裂能达到了110.8 kJ,比基准混凝土的90.8 kJ提高了22%,而聚酯纤维混凝土的断裂能则达到了140.5 kJ,比基准混凝土提高了54.7%.
参考文献
| [1] | 赵国藩.高性能混凝土发展简介[J].施工技术,2002(04):1-2,16. |
| [2] | Carolyn Dry;Mindy Corsaw .A comparison of bending strength between adhesive and steel reinforced concrete with steel only reinforced concrete[J].Cement and Concrete Research,2003(11):1723-1727. |
| [3] | An Yan;Keru Wu;Xiong Zhang .A quantitative study on the surface crack pattern of concrete with high content of steel fiber[J].Cement and Concrete Research,2002(9):1371-1375. |
| [4] | Bing Chen;Keru Wu;Wu Yao .Conductivity of carbon fiber reinforced cement-based composites[J].Cement & concrete composites,2004(4):291-297. |
| [5] | 李仕群,张国辉,张宁,刘飚,曹伟,胡佳山.CaO-Al2O3-P2O5三元系统富铝区水硬活性的研究[J].硅酸盐学报,1998(02):142-149. |
| [6] | 李仕群,苏磊,翟国芳,衣朝华,刘飚,胡佳山.复合磷铝酸盐-硅酸盐水泥的早期水化行为[J].硅酸盐通报,2005(01):20-24. |
| [7] | 衣朝华 .磷铝酸盐-硅酸盐复合水泥耐久性研究[D].济南大学,2006. |
| [8] | 王伟,李仕群,赵发伟,衣朝华,刘飚,胡佳山.玻璃纤维增强磷铝酸盐水泥的初步研究[J].混凝土与水泥制品,2006(04):46-48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%