研究了Ti-26合金固溶处理后,在不同时效温度条件下次生α相的析出特征以及室温拉伸性能.结果表明,在450～650℃范围内时效处理时,随着时效温度的升高,α相析出的体积分数先增多而后减少,Ti-26合金的抗拉强度与α相的体积分数也同样有着先升高而后减少的变化趋势.由于不同体积分数的α相对应着不同的抗拉强度与伸长率,所以,通过时效温度的调整可以使Ti-26合金得到不同抗拉强度与伸长率的配合,以适合不同的使用要求.
参考文献
| [1] | 张庆玲,王庆如,李兴无.航空用钛合金紧固件选材分析[J].材料工程,2007(01):11-14,18. |
| [2] | Misra A;Gibala R;Noebe R D .Optimization of toughness and strength in multiphase inennetallics[J].Intermetallics,2001,9(10-11):971-978. |
| [3] | Z. Xue;Y. Huang;M. Li .Particle size effect in metallic materials: a study by the theory of mechanism-based strain gradient plasticity[J].Acta materialia,2002(1):149-160. |
| [4] | J.F. Nie .Effects of precipitate shape and orientation on dispersion strengthening in magnesium alloys[J].Scripta materialia,2003(8):1009-1015. |
| [5] | O.M. Ivasishin;RE. Markovsky;S.L. Semiatin;C.H. Ward .Aging response of coarse- and fine-grained β titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):296-305. |
| [6] | T. Furuhara;T. Maki;T. Makino .Microstructure control by thermomechanical processing in β-Ti-15-3 alloy[J].Journal of Materials Processing Technology,2001(3):318-323. |
| [7] | 沈桂琴;王世洪;梁佑明 等.Ti-15V-3Cr-3Sn-3AI合金的等温转变研究[J].金属热处理学报,1996,17(01):10-15. |
| [8] | 侯世耀,王平,雷家峰,刘羽寅,刘建荣.固溶时效处理对Ti-15-3合金显微组织及力学性能的影响[J].金属热处理,2007(04):23-26. |
| [9] | 葛鹏,赵永庆,周廉.Ti-B20钛合金的时效特征[J].中国有色金属学报,2005(01):44-48. |
| [10] | 于腾,王磊,赵永庆,王红才,耿可屏,倪浩天.近β型高强钛合金Ti-26的β晶粒长大行为[J].郑州大学学报（工学版）,2009(01):6-9. |
| [11] | 张喜燕;赵永庆;白晨光.钛合金及应用[M].北京:化学工业出版社,2005:93-99. |
| [12] | S. Malinov;W. Sha;Z. Guo .Synchrotron X-ray diffraction study of the phase transformations in titanium alloys[J].Materials Characterization,2002(4):279-295. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%