以WC合金作为电极,氩气为保护气体,采用电火花沉积技术在40Cr钢表面沉积WC合金层,通过显微硬度计、扫描电镜(SEM)及能谱分析(EDS),X射线衍射等测量方法,研究了40Cr钢表面电火花沉积WC层的显微硬度、表面状态、界面行为及相结构组成.结果表明,WC合金电火花沉积层存在微裂纹及气孔,主要由W、Fe6W6C、Fe3C和Cr23C6等相组成；沉积层显微硬度达820 HV,为基体的4.5倍；沉积层断面连续、致密,厚度为30 μm；沉积层与基体之间发生了元素的相互扩散与合金化过程,呈冶金结合,无明显界面.
参考文献
| [1] | 汪瑞军,钱乙余,刘军.Interface behavior study of WC92-Co8 coating produced by electrospark deposition[J].中国焊接(英文版),2004(01):61-64. |
| [2] | J. Tusek;L. Kosec;T. Muhic .ELECTROSPARK DEPOSITION FOR DIE REPAIR[J].Metalurgija,2012(1):17-20. |
| [3] | 高玉新,赵程,易剑.粉末预置法电火花沉积WC-8Co涂层分析[J].焊接学报,2012(03):49-52. |
| [4] | Belik V D;Litvin R V;Kovalchenko M S .Effect of substrate temperature on the electrospark deposition,structure,and mechanical properties of coatings[J].Powder Metallurgy and Metal Ceramic,2012,50(09):698-703. |
| [5] | ZHANG Kun,何业东,WANG De-ren.电火花沉积MCrAlY涂层及其高温氧化行为[J].材料热处理学报,2008(04):143-147. |
| [6] | Le(s)njak Andrej;Tu(s)ek Janez .Some characteristics of electrospark deposition[J].Materials Research and Advanced Techniques,2003,94(11):1260-1266. |
| [7] | E. I. Zamulaeva;E. A. Levashov;A. E. Kudryashov .EFFECT OF WC-Co ELECTRODE STRUCTURE ON THE RATE OF ELECTROSPARK COATING DEPOSITION[J].Metallurgist,2012(9/10):628-633. |
| [8] | 于华,潘清华,李兆楠,林耀华,聂书才,杨豫川.35CrMo钢表面电火花沉积WC合金涂层的界面行为[J].材料热处理学报,2010(10):96-99. |
| [9] | 何鹏,吴承东,钱乙余,汪瑞军.钛合金表面电火花沉积WC电极的粘连行为分析[J].焊接学报,2006(04):25-28,104. |
| [10] | 王建升,高玉新,张瑞珠.铸钢材料电火花表面沉积WC-4Co涂层的组织与性能[J].材料热处理学报,2010(12):123-128. |
| [11] | 罗成,熊翔,董仕节.电火花沉积法在铜电极表面制备TiB2/Ni涂层[J].中国有色金属学报（英文版）,2011(02):317-321. |
| [12] | 郝建军,卜志国,赵建国,刘洪杰,马跃进.TC4钛合金电火花沉积反应合成Ti（CN）涂层[J].材料科学与工艺,2009(03):406-409. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%