利用背散射电子衍射（EBSD）技术,研究了不同连续退火温度下Ti-IF钢微观取向的演变规律,并对不同退火温度下退火板的力学性能进行研究。研究发现当退火温度较低时（780℃）织构分布相对随机,随退火温度升高,ND∥〈111〉织构比例增加,在860℃退火时得到的r值最高,同时ND∥〈111〉织构比例最高,但当退火温度继续升高到900℃时,所有取向的晶粒均得到发展,使ND∥〈111〉织构比例和退火板的r值降低。
Micro-orientations evolution of cold-rolled Ti-IF steel annealed at different temperature was investigated by means of electron back scatter diffraction（EBSD） technique,and the mechanical properties of annealed sheets were studied.The results show that： textures are random distributed at low-temperature（780℃）,with the temperature increasing,ND∥111 texture ratio increases,and the maximum r value and ND∥111 texture ratio at 860℃ are gotten,while the annealing temperature continues to rise to 900℃,all textures are developed,causing the reduce of ND∥111 texture ratio and r value
参考文献
| [1] | 康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009 |
| [2] | 郭艳辉,王昭东,李守卫,邹闻文.IF钢与ELC钢织构及性能的对比[J].东北大学学报（自然科学版）,2007(12):1713-1716. |
| [3] | Bevis HUTCHINSON;Dorota ARTYMOWICZ .Mechanisms and Modelling of Microstructure/Texture Evolution in Interstitial-free Steel Sheets[J].ISIJ International,2001(6):533-541. |
| [4] | 李锋,吕家舜,敖列哥,文伟,张清辉.连续退火工艺对Nb-Ti-IF钢性能及再结晶织构的影响[J].钢铁,2008(01):64-67,72. |
| [5] | 于浩,康永林,傅杰,柳得橹,王中丙,李烈军,范胜标,陈贵江,李柯新.CSP线热轧薄板的组织演变及微观取向研究[J].钢铁,2002(10):38-42. |
| [6] | 王春芳,时捷,王毛球,惠卫军,董瀚.EBSD分析技术及其在钢铁材料研究中的应用[J].钢铁研究学报,2007(04):6-11. |
| [7] | Yasunobu NAGATAKI;Yoshihiro HOSOYA .Origin of the Recrystallization Texture Formation in an Interstitial Free Steel[J].ISIJ International,1996(4):451-460. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%