通过某国产氧化铝粉体的研磨和分散,得到颗粒粒度分布窄、颗粒大小均匀的氧化铝粉体;添加氧化镁为烧结助剂,分别进行无压烧结和真空烧结,研究了烧结温度对氧化铝陶瓷的相对密度、显微结构、抗弯强度和直线透过率的影响.在1 500℃无压烧结样品晶粒尺寸为2-3 μm,抗弯强度达到545 MPa; 1 850℃真空烧结样品的晶粒尺寸为20-30 μm,直线透过率(600 nm)达到32%.
参考文献
| [1] | 李世普.The Special Ceramic Techology(特种陶瓷工艺学)[M].Wuhan:Wuhan Lidustrial University Press,1990:83. |
| [2] | 刘征,高陇桥.俄罗斯真空电子器件用无氧铜的现状和应用[J].真空电子技术,2005(01):62-65. |
| [3] | Ronald G.Munro .Evluated material properties for a sintered α-Alunin[J].Journal of the American Ceramic Society,1997(8):1919-1928. |
| [4] | 高陇桥 .The Progress of High-Pressure Sodium Lamp with Alumina Ceramic Transparent(高压钠灯用氧化铝透明陶瓷的进展)[R].Beijing:Beijing Silicate Society,1999. |
| [5] | A. Braun;G. Falk;R. Clasen .Transparent Polycrystalline Alumina Ceramic with Sub-Micrometre Microstructure by Means of Electrophoretic Deposition[J].Materialwissenschaft und Werkstofftechnik,2006(4):293-297. |
| [6] | Krell A;Hauler T;Klimke J .Transparent Ceramics for Struc-tural Applications:Part 2:Fields of Applications[J].Cfi-Ce-ramic Forum In-teneational,2007,84:E50-E56. |
| [7] | [OL].http://www.baikowskimalakofl:com/upload/produiVpdf_ prod_ 9.pdf |
| [8] | Bodisova K;Sajgalik P .Two-Stage Sintering of Alumina with Submicronmeter Grain Size[J].American Ceramic Society,2007,90(01):330-332. |
| [9] | 彭晓峰;黄校先;张玉峰 .高性能细晶粒氧化铝陶瓷材料的制备与研究[J].无机材料学报,1998(13):327-332. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%