通过在铸轧区的关键部位引入电磁-超声能场,实现对3003铝合金的普通对称铸轧、非对称铸轧和非对称电磁-超声铸轧.用该方法分别制备了上述3种铸轧带坯,并将普通对称铸轧带坯与非对称电磁-超声铸轧带坯加工成厚度为0.25 mm的成品薄带.通过金相显微观察、扫描电镜观察和动静万能试验机测试分析了3种3003铝合金铸轧板的组织和性能.结果表明:与对称铸轧相比,非对称铸轧有效地抑制了宏观偏析,并使铸轧速度提高了33.3％;施加电磁-超声复合能场后,铸轧带坯晶粒显著细化,力学性能明显提高;电磁-超声成品薄带的抗拉强度、屈服强度和伸长率分别比普通成品薄带的提高了32.93％、38.91％和 6.25％.
参考文献
| [1] | 侯 波;李永春;李建荣.铝合金连续铸轧和连铸连轧技术[M].北京:冶金工业出版社,2010:206-207. |
| [2] | 丁培道,蒋斌,杨春楣,方亮.薄带连铸技术的发展现状与思考[J].中国有色金属学报,2004(z1):192-196. |
| [3] | YUN M;LOKYER S;HUNT J D .Twin roll casting of aluminum alloys[J].Materials Science and Engineering A,2000,280(01):116-123. |
| [4] | T. Haga;T. Nishiyama;S. Suzuki .Strip casting of A5182 alloy using a melt drag twin-roll caster[J].Journal of Materials Processing Technology,2003(1/2):103-107. |
| [5] | VIVES C .Effects of electromagnetic vibrations on the microstructure of continuously cast aluminum alloys[J].Materials Science and Engineering A,1993,173(1/2):169-172. |
| [6] | 赵啸林,毛大恒,陈大根.将电磁场引入连续铸轧的新技术探讨[J].中国有色金属学报,1995(04):145-149. |
| [7] | 毛大恒;肖立隆;丁道廉 .电磁场对铸轧板织构和力学性能的影响[J].中南大学学报(自然科学版),1998,29(06):573-576. |
| [8] | Ramirez A;Qian M;Davis B;Wilks T;StJohn DH .Potency of high-intensity ultrasonic treatment for grain refinement of magnesium alloys[J].Scripta materialia,2008(1):19-22. |
| [9] | 李建平,胡建冰,毛大恒,赵冠中.超声波辅助铸轧AZ31镁合金板带的实验研究[J].华中科技大学学报（自然科学版）,2010(12):126-128,132. |
| [10] | 张新明,吴文祥,蹇雄,周卓平.退火过程中AA3003铝合金的析出行为[J].中国有色金属学报,2005(05):675-679. |
| [11] | 张新明,蹇雄.中间退火前后冷轧变形量对3003铝合金阴极箔比电容的影响[J].中国有色金属学报,2005(03):334-337. |
| [12] | MAO Da-heng,ZHANG Yun-fang,NIE Zhao-hui,LIU Qiao-hong,ZHONG Jue.Effects of ultrasonic treatment on structure of roll casting aluminum strip[J].中南工业大学学报(英文版),2007(03):363-369. |
| [13] | ALEXANDER D T L;GREER A L .Solid-state intermetallic phase transformations in 3xxx aluminum alloys[J].Acta Materialia,2002,50(10):2571-2583. |
| [14] | Chen SP.;Kuijpers NCW.;van der Zwaag S. .Effect of micro segregation and dislocations on the nucleation kinetics of precipitation in aluminium alloy AA3003[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):296-306. |
| [15] | 张永皞,张志清,林林.3xxx系罐身铝合金第二相及其对加工过程的影响研究进展[J].材料导报,2012(13):101-108. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%