首先在聚氨酯泡沫基体表面化学镀一层铜，然后电沉积铁，再对聚氨酯进行不同方式的热解，最后对泡沫铁进行还原热处理，研究了热处理工艺对泡沫铁结构与性能的影响，以及热解方式对泡沫铁性能的影响。结果表明：在氮气中热解聚氨酯基体可以有效减少泡沫铁的氧化，获得更好的力学性能；在相变温度以上进行热处理可以有效消除泡沫铁的脆性，减少缺陷；在960℃左右的还原气氛中保温处理2h，可使泡沫铁获得较好的力学性能。
A layer of copper was coated on polyurethane foam substrate surface by chemical plating first, and iron electro-deposition was followed, then the polyurethane was pyrolysed, and finally, the foam iron was heated under a reduced atmosphere. The effect of heat treatment on the structure and properties of foamed iron and the effect of pyrolysis on properties of the foam iron were studied. The results show that the mechanical properties of the foam iron could be enhanced when the polyurethane was pyrolysed in nitrogen atmosphere. It could effectively make foam iron eliminating brittleness and reducing defects when the heat treatment was performed above phasetransition temperature; and fairly good mechanical properties could be obtained after the foam iron was treated at 960 ℃ for 2 h in reducing atmosphere.
参考文献
| [1] | A. Rabiei;L.J. Vendra .A Comparison Of Composite Metal Foam's Properties And Other Comparable Metal Foams[J].Materials Letters,2009(5):533-536. |
| [2] | A.H. Brothers;D.C. Dunand .Amorphous Metal Foams[J].Scripta materialia,2006(4):513-520. |
| [3] | John Banhart .Manufacture, characterization and application of cellular Metals and metal foams[J].Progress in materials science,2001(6):559-632. |
| [4] | X. Badiche;S. Forest;T. Guibert;Y. Bienvenu;J. -D. Bartout;P. Ienny;M. Croset;H. Bernet .Mechanical properties and non-homogeneous deformation of open-cell nickel foams: application of the mechanics of cellular solids and of porous materials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):276-288. |
| [5] | 王芳,王录才.泡沫金属的研究与发展[J].铸造设备研究,2000(03):48-51. |
| [6] | 左正忠,李卫东,胡进,冯祥明,吴慧敏,梁国柱,袁国伟,詹益腾.全光亮镀铁工艺的研究[J].武汉大学学报(理学版),2001(06):697-702. |
| [7] | 赵鹏,浦玉萍,黄春晖,吕广庶.超声波对聚氨酯泡沫塑料化学镀铜的影响[J].材料工程,2008(04):43-46. |
| [8] | 吴伟 .泡沫铁材料的制备及其性能的研究[D].燕山大学,2010. |
| [9] | 孙路阳,侯广亚,曹华珍,郑国渠.电化学沉积法制备泡沫铁及其性能研究[J].浙江工业大学学报,2010(05):508-513. |
| [10] | 陈红辉,朱爱平,夏健康,刘纯辉,高原.泡沫铁制备工艺的研究[J].电镀与环保,2007(05):11-12. |
| [11] | 陈红辉,郝胜策,高原,张婷.超声波对泡沫铁结构的影响[J].电镀与环保,2009(03):15-17. |
| [12] | 徐临超.电流波形对铁电镀层结构和性能的影响[J].电镀与涂饰,2010(09):5-8. |
| [13] | 宫凯,黄因慧,田宗军,刘志东,陈劲松,初晓辉.喷射电沉积制备多孔金属镍工艺[J].机械工程材料,2008(08):40-42,46. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%