借助X射线衍射仪和内耗仪分别研究了低碳铝镇静软质镀锡钢板在热轧、冷轧、连退、平整和镀锡过程中的织构和固溶碳含量变化。结果表明：随着生产工序的进行，{001}〈110〉织构由强变弱，而7纤维织构，尤其是{111}〈112〉织构由弱变强；热轧板经冷轧后的碳固溶量明显降低，而退火加热又使固溶碳含量略有回升，平整又导致固溶碳含量进一步降低，镀锡过程的加热再次造成固溶碳含量略增。
The texture and carbon solution of low carbon Al-killed steel tinplate during hot rolling, cold rolling, continuous annealing, temper rolling and tinning were studied by X-ray diffraction and ini:ernal friction inverted torsion pendulum. The results show that the intensity of {001} 〈110〉 texture decreased during production process, while the "/fiber texture, mainly { 111 } 〈 112 〉 texture, increased. The carbon solution decreased after the hot rolled plate was cold rolled and increased slightly after annealing, and then the carbon solution further decreased after temper rolling, and increased slightly again because heating during tinning process.
参考文献
| [1] | 班必俊,孙震.连退镀锡板的抗时效生产技术[J].上海金属,2007(05):196-198. |
| [2] | 刘书.提高镀锡板T-4CA材抗时效性能措施的试验研究[J].宝钢技术,2006(01):56-58. |
| [3] | 王晓东,黄久贵,李建中,田彦文,刘常升.国内外镀锡板生产发展状况[J].上海金属,2008(04):45-48. |
| [4] | 宋加.我国镀锡板生产技术的发展及几点建议[J].轧钢,2007(02):35-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%