使用传统蜡基粘结剂和改进型蜡基粘结剂分别研究了Ti(C,N)基金属陶瓷粉末注射成形,热脱脂和溶剂脱脂+热脱脂工艺过程,其中包括根据粘结剂TGA制定并优化热脱脂的工艺曲线、不同的溶剂和温度对溶剂脱脂的影响、后续热脱脂工艺路线的确定.结果表明:使用改进型蜡基粘结剂的2#试样热脱脂工艺简单、周期短并易于控制;2#溶剂脱脂率明显高于使用传统蜡基粘结剂的1#试样;经过溶剂脱脂+热脱脂,1#试样脱脂率达到93%,2#试样脱脂率达到96%以上;1#烧结试样的抗弯强度为700 MPa左右,2#则达到1300 MPa,从烧结样品抗弯断口和显微组织的SEM图片得到了验证.Ti(C,N)基金属陶瓷注射成形采用改进型蜡基粘结剂比传统蜡基粘结剂脱脂效果好、力学性能高,改进型蜡基粘结剂更适合Ti(C,N)基金属陶瓷注射成形.
参考文献
| [1] | German R M.Powder Injection Molding[A].Princeton,New Jersey,1990 |
| [2] | Bankovic D R;German R M.Optimization of debinding cycles in Powder Injection Molding[A].MPIF,Princeton,1990 |
| [3] | Hwang K S .[J].REVIEWS IN PARTICULATE MATERIALS,1996,4:71. |
| [4] | Li Songlin,Huang Baiyun,Qu Xuanhui,Li Yimin.Solvent de-binding of water-soluble binder in powder injection moulding[J].中国有色金属学会会刊（英文版）,1999(03):578-581. |
| [5] | Martyn M T;James P T et al.Injection moulding of hardmetal components[J].MPR,1988,43(12):817. |
| [6] | Zhang Shanyong .Titanium carbonitride-based cermets:processes and properties[J].MATERIAL SCIENCE AND ENGINEERING,1993,A163:141. |
| [7] | 刘宁.钇对金属陶瓷力学性能和组织的影响[J].中国稀土学报,1997(01):80. |
| [8] | Qi F.;Kang S. .A study on microstructural changes in Ti(CN)-NbC-Ni cermets[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):276-285. |
| [9] | Park Y J;Kim S W;Kang S .The formation of a solid solution band at the surface of Ti(C,N)-based cermets[J].MATERIAL SCIENCE AND ENGINEERING,2000,A291(1-2):198. |
| [10] | 范畴 .Ti(C,N)基金属陶瓷粉末注射成形的研究[D].武汉:华中科技大学,2005. |
| [11] | 熊惟皓 .颗粒型复合硬质材料微观组织与界面结构的研究[D].华中理工大学,1994. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%