Alumina specimens were joined together with thin aluminium interlayer at 750 and 900°C under different applied pressures and holding time in air. Flexural strength of the joints was then measured using a standard four-point bend test method. Characterization of the interface was carried out to correlate the increase in flexural strength with the applied pressure, holding temperature and time. The study showed that the strength of joint is affected by all three parameters, i.e., processing temperature, holding time as well as applied pressure.
参考文献
| [1] | A. H. Carim;C. H. Mohr .Brazing of alumina with Ti_4CU_2O and Ti_3CU_3O interlayers[J].Materials Letters,1997(3/4):195-199. |
| [2] | A.Meier;P.R.Chidambaram;G.R.Edwards .Modelling of the spreading kinetics of reactive brazing alloys on ceramic substrates: copper-titanium alloys on polycrystalline alumina[J].Acta materialia,1998(12):4453-4467. |
| [3] | N. Shao;J.W. Dai;G.Y. Li .Effect of La on the wettability of Al_2O_3 by molten aluminum[J].Materials Letters,2004(14):2041-2044. |
| [4] | J.T. McKeown;J.D. Sugar;R. Gronsky .Effects of impurities on alumina-niobium interfacial microstructures[J].Materials Characterization,2006(1):50-57. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%