Creep Deformation and Rupture in Smooth and Notched Specimens in HK40 Steel

材料科学技术（英文）, 1989, 5(6): 421-425.

Creep Deformation and Rupture in Smooth and Notched Specimens in HK40 Steel

ZHU Shijie , ZHAO Jie , WANG Fugang , CAO Zhiben Dalian University of Technology , Liaoning , China. To whom correspondence should be addressed.

Keywords： creep , null , null , null

The effects of the eutectic carbides rand secondary carbides on creep deformation and rupture in smooth bars and CT specimens have been studied. The results show that the resistance of the eutectic carbides of skeleton shape to crack growth is larger than that of the blocky shape carbides. The dendritic segregation of secondary carbides promotes the creep ductility. As the secondary carbide particles become coarser, the creep ductility increases and the crack growth rate decreases. However, if the size of secondary carbide is too large, the creep strength decreases too much and therefore crack growth rate increases.

参考文献

[1]
[2]

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
ZHU Shijie ZHAO Jie WANG Fugang CAO Zhiben Dalian University of Technology Liaoning China. To whom correspondence should be addressed.
在百度学术搜索
ZHU Shijie ZHAO Jie WANG Fugang CAO Zhiben Dalian University of Technology Liaoning China. To whom correspondence should be addressed.
在万方数据库搜索
ZHU Shijie ZHAO Jie WANG Fugang CAO Zhiben Dalian University of Technology Liaoning China. To whom correspondence should be addressed.
在CNKI搜索
ZHU Shijie ZHAO Jie WANG Fugang CAO Zhiben Dalian University of Technology Liaoning China. To whom correspondence should be addressed.

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Creep Deformation and Rupture in Smooth and Notched Specimens in HK40 Steel

参考文献