通过BET,XRD,XPS,IR和TPR等表征手段,考察了制备方法对CH4-CO2重整用镍基催化剂物性结构和还原性能的影响.与浸渍的超细载体二元NiO-Al2O3及浸渍的普通载体三元NiO-La2O3-Al2O3催化剂相比,采用溶胶-凝胶法和超临界干燥技术制备的超细二元和三元气凝胶超细催化剂具有高表面积、高孔隙率及孔结构可控等特点,且组分之间的相互作用强,分布均匀,较低温度下即可形成NiAl2O4尖晶石结构,吸附能力强,还具有更丰富的表面缺陷和暴露原子数等纳米材料特性.同时,该方法适宜于制备负载多组分金属催化剂,有利于发挥助剂的改善调节作用,满足CH4-CO2重整反应对催化剂的要求.
参考文献
| [1] | Ashcroft A T;Cheetham A K;Green M L H et al.[J].Nature,1991,352(6332):225. |
| [2] | Erd helyi A;Cserenyi J;Solymosi F .[J].Journal of Catalysis,1993,141(01):287. |
| [3] | Rostrup-Nielsen J R;Bak Hansen J H .[J].Journal of Catalysis,1993,144(01):38. |
| [4] | Bradford M C J;Vannice M A .[J].Preprints-American Chemical Society,Division of Petroleum Chemistry,1997,42(03):604. |
| [5] | Osaki T;Horiuchi T;Suzuki K et al.[J].Applied Catalysis A:General,1997,155(02):229. |
| [6] | Claridge JB.;Brungs AJ.;Marquez-Alvarez C.;Sloan J.;Tsang SC.;Green MLH.;York APE. .New catalysts for the conversion of methane to synthesis gas: Molybdenum and tungsten carbide[J].Journal of Catalysis,1998(1):85-100. |
| [7] | Pajonk G M .[J].Applied Catalysis,1991,72(02):217. |
| [8] | Schneider M;Baiker A .[J].Catalysis Review-Science and Engineering,1995,37(04):515. |
| [9] | Pajonk G M .[J].Catalysis Today,1997,35(03):319. |
| [10] | Gonzalez R D;Lopez T;Gomez R .[J].Catalysis Today,1997,35(03):293. |
| [11] | 李泉;曾广赋;席时权.[J].化学通报,1995(06):29. |
| [12] | 胡泽善;张量渠;郭慎独 .[J].催化学报,1992,13(02):83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%