为了提高热镀锌钢板的耐蚀性,研究了苯并三氮唑(BTA)改性双-[γ-(三乙氧基硅)丙基]四硫化物硅烷(BTESPT)溶液处理热镀锌钢板试样的耐蚀性能和组成,并与未经BTA改性的硅烷处理试样以及铬酸盐钝化试样进行比较.结果表明:BTA作为阴极型缓蚀剂改性硅烷涂层,改性涂层主要以Si-O-Si和Si-O-Zn为主,BTA主要以分子形式存在于硅烷涂层中,以[BTA-Zn2]配位化合物存在于涂层/镀锌基体界面处,从而明显提高了改性硅烷涂层的耐蚀性能;改性硅烷涂层主要含Zn,Si,O,S,C和N元素,N含量的变化趋势表明BTA改性硅烷涂层具有自愈合能力.
参考文献
| [1] | Pinto, R.;Carmezim, M.J.;Ferreira, M.G.S.;Montemor, M.F. .A two-step surface treatment, combining anodisation and silanisation, for improved corrosion protection of the Mg alloy WE54[J].Progress in Organic Coatings: An International Review Journal,2010(2):143-149. |
| [2] | 吴海江,杨飞英,卢锦堂.热镀锌层上改进型硅烷膜的耐蚀性能[J].中国腐蚀与防护学报,2009(02):119-122. |
| [3] | 尤伟,卢锦堂,林碧兰.热镀锌层上磷化/硅烷处理复合膜的耐蚀性研究[J].材料保护,2008(03):34-36,57. |
| [4] | Alexey K;Marie-José C;Didier L .Characterization by different analytical techniques of SiO2 and silane thin films deposited on rough hot-dip galvanized steel surfaces[J].Surface and Coatings Technology,2012,206:2 759 ～ 2 768. |
| [5] | Trabelsi W;Cecilio P;Ferreira MGS;Montemor MF .Electrochemical assessment of the self-healing properties of Ce-doped silane solutions for the pre-treatment of galvanised steel substrates[J].Progress in Organic Coatings: An International Review Journal,2005(4):276-284. |
| [6] | 安江峰;郑鹏华;吴军 等.镀锌钢表面绿色高效硅烷复合膜处理技术研究[J].材料保护,2011,44(4):52 ～55. |
| [7] | 易德莲,王静,李字鹏,刘敏,伍林,庞宽,豆丙乾,李敏敏.镀锌板的复合钝化[J].腐蚀与防护,2010(02):142-145. |
| [8] | 单凤君,齐国超,王双红,孙同明.热镀铝锌钢表面环氧树脂-硅烷复合涂层及其耐蚀性能[J].材料保护,2013(12):7-9. |
| [9] | 张胜涛,薛茗月,王艳波,侯保荣.苯并三氮唑缓蚀剂在铜表面覆盖行为的研究[J].腐蚀科学与防护技术,2006(05):313-316. |
| [10] | 单凤君,刘常升,王双红,齐国超,刘栋.热镀铝锌层铈掺杂硅烷钝化膜的性能[J].材料研究学报,2008(02):197-200. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%