采用4点弯曲试样,对X65钢级UOE焊管焊缝接头进行NACE0177标准规定的SSCC(Sulfur Stress Corrosion Cracking,硫化物应力腐蚀开裂)试验,并采用应变计法完成目标应力加载.结果表明,通过应变计法可以有效地建立FPB(Four Point Bent,4点弯曲)试样加载应变-载荷-应力关系,并根据该关系准确确定目标加载应变量,从而实现目标应力的准确加载.采用该方法完成试验试样90％实际屈服强度的应力加载,并经H2S环境溶液浸泡720h后表面未见裂纹,试验材料表现出优异的抗硫化物应力腐蚀开裂性能.
参考文献
| [1] | 张学元,杜元龙.钢铁发生硫化物应力腐蚀裂开的试验方法与技术[J].材料保护,1995(10):18. |
| [2] | 高惠临.管线钢与管线钢管[M].北京:中国石化出版社,2012 |
| [3] | 方丙炎,王俭秋,朱自勇,韩恩厚,柯伟.埋地管道在近中性pH和高pH环境中的应力腐蚀开裂[J].金属学报,2001(05):453-458. |
| [4] | NACE Standard TM0177.Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments[S].Texas:NACE Interna tional,2005. |
| [5] | ANS/API Specification 5L.Specification for Line Pipe[S].Washington,DC:American Petroleum Institute,2007. |
| [6] | ISO 15166-2.Petroleum and Natural Gas Industries-Materials for Use in H2S-Containing Environments in Oil and Gas Production Part 2:Cracking-resistant Carbon and Low-Alloy Steels,and the Use of Cast Irons[S].Switzerland:International Organization for Standardization,2009. |
| [7] | 鲜宁,姜放,荣明,赵华莱.四点弯曲加载下带焊缝试样表面的最大拉应力公式推导与分析[J].理化检验-物理分册,2010(07):415-418. |
| [8] | 刘家泳,汪尧,戈晓,张丽敏,张冬梅,刘学志.四点弯曲试验研究[J].物理测试,2010(02):44-47. |
| [9] | 单辉祖.材料力学[M].北京:国防工业出版社,1986 |
| [10] | 梅维勒RA;芬尼I;勾佛仪.由弯曲试验求单轴应力应变曲线[J].水利水电科技进展,1983(03):16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%