针对不同方法制备的AZ31镁合金薄板,利用热拉伸试验机和金相显微镜对其在不同温度和变形速率下的流变应力进行了实验研究.结果表明:挤压、交叉、热轧和冷轧等方法制备的AZ31镁合金薄板的应力-应变曲线基本特征是相同的.峰值流变应力随变形温度的升高和应变速率的降低而降低,在低温时具有明显的厚度效应;当温度大于350℃时峰值流变应力几乎不随板材厚度变化而变化;应变速率小于1.0 ×10~(-2) s~(-1),变形温度大于150℃下所有AZ31薄板的延伸率均δ≥45%;单向轧制薄板的各向异性随温度提高减小.
Flow stress of different temperature and deformation rate on AZ31B magnesium alloy sheets of different preparation method was studied by tensile test machine and metalloscope. The results show the basic characteristics of stress-strain curves of AZ31 magnesium alloy sheets prepared by extrusion, cross rolling, hot rolling and cold wiling is the same. Peak flow stress reduces with strain rate decreases and deformation temperature increases.There is obvious thickness effect on peak flow stress at low temperature; the peak flow stress is almost no aherative with the sheet thickness changes at the temperature higher than 350 ℃; the elongation of AZ31 magnesium alloy sheet is more than 45% at strain rate less than 1.0 x 10~(-2)s~(-10 and deformation temperature higher than 150 ℃; ani-sotropy of longitudinal roiling sheet reduces with the temperature increases.
参考文献
| [1] | 张青来,胡永学,王粒粒,孙毓蔚,周娅莉.挤压后交叉轧制的镁合金薄板组织研究[J].热加工工艺,2007(09):1-5. |
| [2] | 余琨,黎文献.Mg-Al-Zn系变形镁合金轧制及热处理后的组织和性能[J].金属热处理,2002(05):8-11. |
| [3] | 苌群峰,李大永,彭颖红,曾小勤.AZ31镁合金板材温热冲压数值模拟与实验研究[J].中国有色金属学报,2006(04):580-585. |
| [4] | 郭强,严红革,陈振华,张辉.AZ31镁合金高温热压缩变形特性[J].中国有色金属学报,2005(06):900-906. |
| [5] | 刘晓霏,严巍,陈国学.AZ31B镁合金塑性变形动态再结晶的实验研究[J].塑性工程学报,2005(03):10-13. |
| [6] | 王智文,张治民,王强,张宝红.AZ31变形镁合金等温变形力学特性的研究[J].机械工程与自动化,2005(01):40-42,44. |
| [7] | 刘楚明,刘子娟,朱秀荣,周海涛.镁及镁合金动态再结晶研究进展[J].中国有色金属学报,2006(01):1-12. |
| [8] | J. C. Tan;M. J. Tan .Superplasticity in a rolled Mg-3Al-1Zn alloy by two-stage deformation method[J].Scripta materialia,2002(2):101-106. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%