采用SEM和XRD方法对CSP冷轧冲压用钢薄板坯和热轧板氧化皮进行了研究.结果表明,覆盖在板坯表面的氧化皮对高温腐蚀有明显保护作用,均热前后Fe_2O_3:Fe_3O_4:FeO质量分数比值为5:35:60,新鲜基体腐蚀严重些,Fe_2O_3和Fe_3O_4质量分数分别增加到28%和64%.卷取后快冷钢的氧化皮以2层结构为主,Fe_2O_3:Fe_3O_4:FeO质量分数比值为6:31:63,缓冷钢的氧化皮中析出了弥散或薄片状的Fe相,Fe_2O_3:Fe_3O_4:FeO:Fe质量分数比值为8:73:15:4,二者厚度相差不大.卷取温度升高,缓冷钢中残余FeO明显减少,不利于酸洗.
The oxide scale on both thin slab and hot rolled strip for cold rolled steel has been studied by XRD and SEM.It was found that oxide scale prior to soaking can protect obviously thin slab from high temperature corrosion of oxidation gas.After soaking Fe_2O_3:Fe_3O_4:FeO is 5:35:60,content of Fe_2O_3 and Fe_3O_4 are 28%and 64%,respectively.oxide scale of strip with quick cooling after coiling comprises mainly two layer structure and Fe_2O_3:Fe_3O_4:FeO is 6:31:63.For the strip with slow cooling,new dispersed or lamellate Fe phase precipitates and Fe_2O_3:Fe_3O_4:FeO:Fe is 8:73:15:4.There is no distinct difference of thickness between two oxide scale.However,for those strip with slow cooling after coiling,content of remained FeO of oxide scale obviously decreases,which is unfavorable to pickling.
参考文献
| [1] | Klaus Schwerdtfeger;Shunxin Zhou .A Contribution to Scale Growth during Hot Rolling of Steel[J].Steel Research,2003(9):538-548. |
| [2] | Chen R Y;Yuen W Y D .Oxide-Scale Structures Formed onCommereial Hot-Rolled Steel Strip and Their Formation Me-chanisms[J].Oxidation of Metals,2001,56(01):89. |
| [3] | 于洋,李庆亮,刘振宇.热轧带钢氧化铁皮生长过程数值模拟[J].钢铁,2008(01):55-57. |
| [4] | 石杰,王德仁,何业东,齐慧滨.用CO还原BRC3热轧带钢表面氧化铁皮的研究[J].钢铁,2008(05):89-92. |
| [5] | Chen R Y;Yuen W Y D .A Study of the Scale Structure of Hot-Rolled Steel Strip by Simulated Coiling and Cooling[J].Oxidation of Metals,2000,53(05):539. |
| [6] | 邓伟,张宇,杨大正,徐大勇,刘常鹏,刘玉良.钢坯氧化烧损影响因素试验研究[J].冶金能源,2006(06):39-40,50. |
| [7] | Mikkelsen L;Linderoth S .High Temperature Oxidation of Fe-Cr Alloy in O_2-H_2-H_2O Atmospheres Microstructure and Kinetics[J].Materials Science and Engineering,2003,361(01):198. |
| [8] | 章华明,车彦民,陈其安,朱涛,贺子凯.CSP热轧板卷氧化皮结构[J].钢铁,2006(06):67-70. |
| [9] | SUN Wei-hua;Tieu A K;JIANG Zheng-yi .Oxide Scales Growth of Low-Carbon Steel at High Temperatures[J].Journal of Materials Processing Technology,2004,155:1300. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%