评述了奥氏体不锈钢在连多硫酸溶液中的应力腐蚀开裂叙述环境、钢中碳含量、热处理、应力等因素的作用.讨论防止应力腐蚀计裂的措施
This paper presents a review of stress corrosion cracking(SCC)of austenitic stain-less steels in polythionic acid solution.The influences of several factors,such as environment,car-bon content in the steel,heat treatment and stress are described.The mecha
参考文献
| [1] | |
| [2] | DravnleksandSamansCHProc．API．1957．VoL．37,SectionIII.1002HellerJJandprescottGRMaterialsProtection,1965、4(9):14．3PrescottGR,BraunCFandHellerJJ．MaterialsProtection,1968．7(3):424段学章,张琦炼油设计,1989,(6):315余B年,张洪惠物理测试,1991,(3):60．6段学章,叶棣物理测试,1991,(1):427林秀机不锈钢汇编中国金属学会特殊钢学术委员会不锈钢专业组,1985678小着正伦著袁宝林等译金属的腐蚀破坏与防蚀技术北京:化学工业出版社,1988,4309VermaKM,VermaSC．SinhaAK．Br．CorrosionJ．1982．17(4):315．10松岛严防食技术,1973,22(4):14111小若正伦,工藤纠夫日本金属学会志,1979,43(7):59512Ahmads,MentaMLCorrosion．1983．39(8):33013段学章,许素珍,李铁藩中国腐蚀与防护学报,1990．10(3) |