通过扫描电子显微镜(SEM)、电子背散射衍射(EBSD)、取向成像显微技术(OIM)研究了在不同冷轧及退火工艺下Ni-Cr-W系高温合金晶界特征分布的规律.结果表明,70%变形量下再结晶完成所需时间较短,特殊晶界比例随着退火时间延长先增加后减少;10%变形量下再结晶驱动力较小,再结晶所需时间较长,特殊晶界比例在长时间退火后达到最大值.在晶粒团簇内部,晶粒之间有∑3n的取向关系,而不同的晶粒团簇间,晶粒则没有这种特殊的取向关系.
参考文献
[1] | Randle V.The Role of the Coincidence Site Lattice in Grain Boundary Engineering[M].Michigan:Institute of Materials,1996 |
[2] | Sauttera H;Gleitera H;B(a)ro G .[J].Acta Metallurgica,1977,5(04):467. |
[3] | Laws M S;Goodhew P J .[J].Acta Metallurgica,1991,39(07):1525. |
[4] | Qian X R;Chou Y T .[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1985,52(02):113. |
[5] | Yamamoto Y.;Kajihara M.;Mori T.;Moriyama M. .Kinetics of diffusion induced grain boundary migration of [100] twist boundaries in the Cu(Zn) system[J].Acta materialia,1999(6):1757-1766. |
[6] | Zhou Y;Aust K T;Erb U et al.[J].Scripta Materialia,2001,45:49. |
[7] | Lehockey E M;Palumbo G .[J].Materials Science and Engineering,1997,A237(02):168. |
[8] | Alexandreanu B;Was G S .[J].Scripta Materialia,2006,54(06):1047. |
[9] | Shimada M;Kokawa H;Wang Z J et al.[J].Acta Materialia,2002,50(09):2331. |
[10] | Watanabe T .[J].Res.Mechanica,1984,11:47. |
[11] | Berger A;Wilbrant P J;Ernst F .[J].Progress in Materials Science,1998,32:1. |
[12] | 夏爽 .Study on the Grain Boundary Character Distribution and Its Evolution Mechanism in Alloy 690(690合金中晶界特征分布及其演化机理的研究)[D].上海:上海大学,2007. |
[13] | Gertsman V Y;Henager C H .[J].Interface Science,2003,11:403. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%