研究5%~7%(体积分数,下同)ZrO2颗粒增强Zr55Cu30Al10Ni5非晶复合材料的微观组织和压缩断裂行为.非晶基体的断裂形貌主要以脉状形貌为主,而复合材料的断口形貌中除了脉状形貌外还有平滑区存在.当ZrO2颗粒的含量达到7%时,其断裂强度也由基体的1716MPa增加到2138MPa.但是由于ZrO2颗粒的添加在基体中产生了Cu10Zr7和CuZr脆性相,因而复合材料没有产生明显的塑性.

The microstructure and fracture behavior of Zr55Cu30Al10Ni5 monolithic glass and Zr55Cu30Al10Ni5 reinforced with 5%-7% ZrO2 particles composites have been studied. Vein-like pattern is the main fracture morphology of the matrix, while the smooth regions can be observed on the composites fracture surface besides vein-like pattern. The fracture strength increases from 1716 MPa to 2138 MPa after adding 7vol% ZrO2particles with average particle size of 1 μm into the matrix, but the composites show no visible plasticity due to formation of Cu10Zr7 and CuZr phases in the matrix.

参考文献

[1] Wang WH;Dong C;Shek CH .Bulk metallic glasses[J].Materials Science & Engineering, R. Reports: A Review Journal,2004(2/3):45-89.
[2] Hui X;Dong W;Chen G L et al.[J].Acta Materialia,2007,55:907.
[3] Kato H;Inoue A .[J].Materials Transactions-Japan Institute of Metals,1997,38:793.
[4] Hays CC.;Johnson WL.;Kim CP. .Microstructure controlled shear band pattern formation and enhanced plasticity of bulk metallic glasses containing in situ formed ductile phase dendrite dispersions[J].Physical review letters,2000(13):2901-2904.
[5] Eckert J;Kühn U;Mattern N et al.[J].Intermetallics,2002,10:1183.
[6] Ying-Kun Xu;Han Ma;Jian Xu et al.[J].Acta Materialia,2005,53:1857.
[7] Fan C;Inoue A .[J].Applied Physics Letters,2000,77:46.
[8] Inoue A;Zhang T .[J].Materials Transactions-Japan Institute of Metals,1996,37:185.
[9] Lewandowski JJ;Greer AL .Temperature rise at shear bands in metallic glasses[J].Nature materials,2006(1):15-18.
[10] Herlmaiser M .[J].Journal of Materials Processing Technology,2001,117:374.
[11] Kusy M;Concustell A;Gebert A et al.[J].Intermetallics,2006,14:928.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%