Tensile tests of GH4169 alloy were performed at room temperature. Different fractions, distributions and shapes of δ phase was prepared by aging treated at 880 °C, 930 °C and 980 °C for 5 h or 10 h. The effect of δ phase on the mechanical pro- perties of GH4169 alloy was investigated. The results show that 0.2% yield strength and ultimate tensile strength of GH4169 alloy increase by 61 MPa and 78 MPa respectively when the fraction of δ phase increases from 2.20% to 5.21%. Then, the ultimate tensile strength remains at 1 012 MPa even when the fraction of δ phase reaches 7.56%. The fraction effect of δ phase on the strength improvement of GH4169 alloy is more signiifcant than morphology, and the critical fraction value is 5.21%. In addition, the elongation decreases by 14.1% when the fraction of δ phase increases from 2.20% to 7.56%. Excessive needle or short rod shaped δ phase is responsible for the reduction of elongation.
参考文献
[1] | N. Zhou;D.C. Lv;H.L. Zhang.Computer simulation of phase transformation and plastic deformation in IN718 superalloy: Microstructural evolution during precipitation[J].Acta materialia,2014:270-286. |
[2] | L.Zheng;M.C.Zhang;R.Chellali;H.Bouchikhaoui J.X.Dong .[J].Materials Science and Technology,2013,28:122-128. |
[3] | Y.C. Lin;Xiao-Min Chen;Dong-Xu Wen;Ming-Song Chen.A physically-based constitutive model for a typical nickel-based superalloy[J].Computational Materials Science,2014:282-289. |
[4] | L.Zheng;M.C.Zhang;R.Chellali;J.X.Dong .[J].Application Surface Sinence,2011,257:9762-9767. |
[5] | L.Zheng;M.C.Zhang;R.Chellali;J.X.Dong .[J].Mater Des,2011,32:1981-1986. |
[6] | Y.Huang;T.G.Langdon .[J].Journal of Materials Science,2007,42:421-427. |
[7] | M.Sundararaman;P.Mukhopadhyay;S.Banerjee .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1992,23:2015-2028. |
[8] | X.P.Wei;W.J.Zheng;Z.G.Song;T.Lei Q.L.Yong Q.C.Xie .[J].J Iron Steel Res Int,2014,21:375-381. |
[9] | Y.Q.Ning;M.W.Fu;X.Chen .[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2012,540:164-173. |
[10] | Y.Wang;W.Z.Shao;L.Zhen;B.Y.Zhang .[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2011,528:3218-3227. |
[11] | G.A.Rao;M.Kumar;M.Srinivas;D.S.Sarma .[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2003,355:114-125. |
[12] | H.Y. Zhang;S.H. Zhang;M. Cheng .Deformation characteristics of 5 phase in the delta-processed Inconel 718 alloy[J].Materials Characterization,2010(1):49-53. |
[13] | H. Y. Zhang;S. H. Zhang;Z. X. Li;M. Cheng .Hot die forging process optimization of superalloy IN718 turbine disc using processing map and finite element method[J].Proceedings of the Institution of Mechanical Engineers, Part B. Journal of engineering manufacture,2010(1):103-110. |
[14] | W.C.Liu;F.R.Xiao;M.Yao .[J].Journal of Materials Science,1997,16:769-771. |
[15] | D.Y.Cai;W.C.Liu;R.B.Li;W.H.Zhang M.Yao .[J].Journal of Materials Science,2004,39:719-721. |
[16] | W. C. Liu;F. R. Xiao;M. Yao;Z. L. Chen;Z. Q. Jiang;S. G. Wang .Relationship between the lattice constant of r phase and the content of δ phase, γ″ and γ′ phases in inconel 718[J].Scripta materialia,1997(1):59-64. |
[17] | F.L.Sui;Y.Zuo;X.H.Liu;L.Q.Chen .[J].Appl Math Modell,2013,37:8776-8784. |
[18] | C.Z.Wang;R.B.Li .[J].Journal of Materials Science,2004,39:2593-2595. |
[19] | W.C.Liu;M.Yao;Z.L.Chen;S.G.Wang .[J].Journal of Materials Science,1999,34:1-4. |
[20] | X.S.Zhou;Y.B.He;J.H.Liu;S.J.Xin,D.Wang,Y.F.Cui,P.Li,Y.Dong .[J].Ordnance Material Science and Engineering,2012,35(06):74-77. |
[21] | H.Y.Zhang.Research on the Control Mechanisms of Microstructure of GH4169 Alloy during the Delta Process and Its Applications[M].Insti-tute of Metal Research,CAS,Shenyang,2010 |
[22] | Y.C.Lin;J.Deng;Y.Q.Jiang;D.X.Wen G.Liu .[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2014,598:251-262. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%