将合成的水性聚氨酯（WPU）与纳米氧化锡锑（ATO）复合,得到了功能性WPU/ATO复合分散体,研究了γ-缩水甘油醚氧丙基三甲氧基硅烷（KH560）的交联反应及其对薄膜性能的影响。FT-IR结果确认了KH560硅醇间的缩合反应,以及KH560的环氧基与WPU中羧基之间的酯化反应。缩合和酯化等反应实现了功能性薄膜的后交联,既显著改善了薄膜的附着力、硬度和耐水性,又保障了良好的透过率和隔热效果。当KH560用量为3.0%（质量分数）,ATO用量为7.0%（质量分数）时,薄膜附着力为0级,硬度达2H,吸水率为10.7%,可见光透过率为70.1%,红外屏蔽率达到66.5%,薄膜满足了透明和隔热的双重要求。
WPU/ATO hybrid dispersion was prepared through synthesized waterborne polyurethane （WPU） and nano antimony tin oxide （ATO） dispersion. The influences of the crosslinking reaction of γ-glycidoxyprop- yltrimethoxy silane （KH560） on the performance of formed films were investigated in paper. FT-IR proves that the condensation reaction between silanol, and the esterification between carboxyl of WPU and epoxy groups in KH560. Functional films were modified with post-crosslinking reaction, and the hardness, adhesion and water resistance were improved effectively, while sufficient transparency and excellent heat insulation performance re- main as well. When the contents of KH560 and ATO are 3.0% and 7.0%, pencil hardness, adhesion force and water absorption reach 2H, 0 degree and 10.7 %, respectively. On the otherhand, the average transmittance for visible light is 70.1% and the shield rate to near infrared light is 66.5 $, therefore exhibiting effective heat-in- sulatability.
参考文献
| [1] | Wang, X.;Hu, Y.;Song, L.;Xing, W.;Lu, H.;Lv, P.;Jie, G. .Effect of antimony doped tin oxide on behaviors of waterborne polyurethane acrylate nanocomposite coatings[J].Surface & Coatings Technology,2010(7):1864-1869. |
| [2] | Song J E;KimY H;Kang Y S .[J].Current Applied Physics,2006,6(04):791-795. |
| [3] | Kaneko S;Sakurai H;Izumi K et al.Active Radiation Ray Curable Solar Radiation Blocking Resin Compositions and Films Coated Therewith[P].USP:6107360,2000-08-22. |
| [4] | Okuhara Y;Kato T;Matsubara H et al.[J].Thin Sol-id Films,2011,519(07):2280-2286. |
| [5] | Wang, X.;Hu, Y.;Song, L.;Xing, W.;Lu, H.;Lv, P.;Jie, G. .Effect of antimony doped tin oxide on behaviors of waterborne polyurethane acrylate nanocomposite coatings[J].Surface & Coatings Technology,2010(7):1864-1869. |
| [6] | 李雪,周斯,吴金丽,任丽,张福强.ATO/WPU复合隔热涂料的制备与性能研究[J].新型建筑材料,2011(08):50-53. |
| [7] | 芦小松,项尚林,赵石林.原位聚合制备纳米氧化锡锑/水性聚氨酯复合乳液及性能表征[J].涂料工业,2008(12):16-19,22. |
| [8] | Lai Xiaojuan;Shen Yiding;Wang Lei et al.[J].Journal of Functional Materials,2011,5(42):940-942. |
| [9] | Bisht H;Eun T;Aegerter A .[J].Thin Solid Films,1999,351(01):109-114. |
| [10] | Garima Jain;R. Kumar .Electrical and optical properties of tin oxide and antimony doped tin oxide films[J].Optical materials,2004(1):27-31. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%