为了提高铸铝表面的防腐蚀和防污能力,通过微弧氧化在铸铝表面原位生长出均匀分布的氧化铝陶瓷膜层,采用长链氟硅烷对微弧氧化陶瓷膜层进行修饰,制备了接触角大于150°的超疏水表面.采用X射线衍射仪(XRD)、扫描电镜(SEM)研究了铸铝微弧氧化陶瓷膜结构和表面形貌,并测试了长链氟硅烷修饰对铸铝以及微弧氧化铸铝表面接触角的影响,探讨了铸铝微弧氧化陶瓷膜层的长烷链氟硅烷修饰机理.通过正交试验确定了正向电压为480 V,占空比为50/50,微弧氧化时间为15 min时,生成的微弧氧化陶瓷膜层具有较为连续和致密的微米级突起结构,经十三氟辛基三乙氧基硅烷修饰后获得接触角高达162.6°的超疏水表面,并且具有一定的持久性和稳定性.
参考文献
| [1] | 张聚国;杨华.LY12铝合金微弧氧化陶瓷膜的性能研究[J].上海有色金属,2009(1):5-8. |
| [2] | Libang Feng;Yanhui Che;Yanhua Liu;Xiaohu Qiang;Yanping Wang.Fabrication of superhydrophobic aluminium alloy surface with excellent corrosion resistance by a facile and environment-friendly method[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013Oct.15(Oct.15):367-374. |
| [3] | 王峰;孙士飞;杨霞.锡青铜表面超疏水薄膜的制备及其水润滑减摩性能[J].材料保护,2015(1):54-56. |
| [4] | Tao Liu;Yansheng Yin;Shougang Chen;Xueting Chang;Sha Cheng.Super-hydrophobic surfaces improve corrosion resistance of copper in seawater[J].Electrochimica Acta,200711(11):3709-3713. |
| [5] | 徐文骥;窦庆乐;孙晶;宋金龙;庞桂兵.基于电化学加工方法的铝基超疏水表面制备技术研究[J].中国机械工程,2011(19):2354-2359. |
| [6] | 李松梅;李彬;刘建华;于美.铝合金表面用化学刻蚀和阳极氧化法制备的超疏水膜层的耐蚀性能[J].无机化学学报,2012(8):1755-1762. |
| [7] | M.Thieme;F.Streller;F.Simon;R. Frenzel;A.J.White.Superhydrophobic aluminium-based surfaces: Wetting and wear properties of different CVD-generated coating types[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013Oct.15(Oct.15):1041-1050. |
| [8] | 李杰;张会臣;高玉周.MB8镁合金疏水/超疏水表面制备与微摩擦特性研究[J].功能材料,2012(22):3063-3069. |
| [9] | 康志新;赖晓明;王芬;龙雁;李元元.Mg-Mn-Ce镁合金表面超疏水复合膜层的制备及耐腐蚀性能[J].中国有色金属学报,2011(2):283-289. |
| [10] | 薛文斌;华铭;施修龄;田华.铸造铝合金微弧氧化膜的生长动力学及耐蚀性能[J].硅酸盐学报,2007(6):731-735. |
| [11] | 戈云杰;宋仁国;王超;郭燕清;陈亮;项南;宋若希.铸铝合金微弧氧化时间对陶瓷膜微观结构及性能的影响[J].材料保护,2015(3):6-8,19. |
| [12] | 刘传生;蒋文曲;管自生.类荷叶结构聚全氟乙丙烯的超疏水性[J].高等学校化学学报,2011(5):1175-1180. |
| [13] | Yang Y.;Chen HL.;Mei YF.;Chen JB.;Wu XL.;Bao XM..Anodic alumina template on Au/Si substrate and preparation of CdS nanowires[J].Solid State Communications,20026/7(6/7):279-282. |
| [14] | 刘元;李兴俊;龚正朋.氧化时间对7A09超高强铝合金微弧氧化陶瓷膜的影响[J].表面技术,2013(2):53-55,73. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%