Tungsten powder was fabricated from the system CaWO4-Mg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have been studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87μn, specific surface area of 1.09m2/g and purity of above 99.0%.
参考文献
| [1] | J Y Li;J Z Huang .[J].Rare Metals,1990,9(04):287. |
| [2] | P Ettmayer .[J].Annual Review of Materials Science,1989,19:145. |
| [3] | A G Merzhanov .[J].Combustion and Flame,1969,13(02):143. |
| [4] | Z A Munir;U A Tamburini .[J].Materials Science Reports,1989,3:277. |
| [5] | Z A Munir .[J].Journal of Materials Science,1986,21(01):251. |
| [6] | Z A Munir;J B Holt .[J].Journal of Materials Science,1987,22(02):710. |
| [7] | S K Ko;C W Won;S S Cho;B.S.Chun .[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1996,27(02):315. |
| [8] | The Teaching and Research Section of Dalian Institue of Technology, Inorganic Chemistry[M].北京:人民教育出版社,1994:274. |
| [9] | A G Merzhanov;A·G·Merzhanov .Combustion Processes in Chemical Technology and Metallurgical[Z].Chemogolovka,1975. |
| [10] | Y L Wang;T A Zhang;H Yang;S.W.Wei .[J].Journal of Advanced Materials,2004,36(02):44. |
| [11] | 王延玲,张廷安,杨欢,魏世丞.自蔓延高温还原法制备钨粉的研究[J].稀有金属材料与工程,2001(04):310-313. |
| [12] | S Y Chen .[J].Journal of Central South Institute of Mining and Metallurgy,1994,25(05):607. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%