就国外近期研究内容,介绍了熔融共混过程初期的形态结构发展模式.在聚合物共混初期,分散相首先形成片状物(带状物),进而在剪切力场作用下碎裂成球形粒子,完全熔融以后,粒径变化很小;此模式对反应性体系和非反应性体系均适合.对于弹性体含量低的橡塑共混体系,在共混初期弹性粒子首先成为连续相,可用一"四阶段"相反转模式描述;对于反应性体系,此模式不会改变,但是相反转延迟发生,并伴有转矩增大现象.

参考文献

[1] Schreiber H P;Olguin A .[J].Polymer Engineering and Science,1983,23:129.
[2] Karger-Kocsis J;Kallo A;Kuleznev V N .[J].Polymer,1984,25:279.
[3] Plochcki A P;Dagli S S;Andrews R D .[J].Polymer Engineering and Science,1990,30:741.
[4] Favis B D .[J].Journal of Applied Polymer Science,1990,39:285.
[5] Scott C E;Macosko C W .[J].Polymer Bulletin,1991,26:341.
[6] Sundararaj U;Macosko C W;Rolando R J et al.[J].Polymer Engineering and Science,1992,32:1814.
[7] Lindt J T;Ghosh A K .[J].Polymer Engineering and Science,1992,32:1802.
[8] Scott CE.;Macosko CW. .MORPHOLOGY DEVELOPMENT DURING THE INITIAL STAGES OF POLYMER-POLYMER BLENDING[J].Polymer: The International Journal for the Science and Technology of Polymers,1995(3):461-470.
[9] Sundararaj U .[D].University of Minnesota,1994.
[10] Sundararaj U.;Macosko CW.;Dori Y. .SHEET FORMATION IN IMMISCIBLE POLYMER BLENDS - MODEL EXPERIMENTS ON INITIAL BLEND MORPHOLOGY[J].Polymer: The International Journal for the Science and Technology of Polymers,1995(10):1957-1968.
[11] Shih C K .[J].Polymer Engineering and Science,1995,35:1688.
[12] Sundararaj U;Macosko C W;Shih C K .[J].Polymer Engineering & Science,1996,13:1769.
[13] Ban L L;Doyle M J;Disko M M et al.[J].Polym Communications,1988,29:163.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%