研究K417G合金及其表面Ni(Co)CrAlYSi涂层在室温大气环境下的磨损特性。结果表明：K417G合金及其表面Ni(Co)CrAlYSi涂层的磨损受磨损亚表层疲劳脱层和磨损表面环境脆性的共同作用，致使其磨损率高于纯Ni的。在磨损过程中，环境脆性逐渐作用于磨损表面，磨损表面的裂纹源在γ/γ′界面以及碳化物与合金基体界面形核，裂纹既沿着γ/γ′面以及碳化物与合金基体界面扩展，又进入γ′晶粒，呈现沿晶和穿晶混合状。
The tribological properties of K417G superalloy and Ni(Co)CrAlYSi coatings/K417G were investigated at room temperature in atmospheric environment. The results show that the worn mechanism of both K417G superalloy and the coatings is due to interaction of environment embrittlement and fatigue delamination in subsurface stratum, which results to the higher wear rate compared with the pure nickel plate. The enviromental embrittlement gradually affect the worn surface during the process of wear. The formation of crack resource on the worn surface begins at both the interface ofγ/γ′ phases and the interface of carbide and alloy. The cracks extend along both the interface ofγ/γ′ phases and the interface of carbide and alloy and enter into theγ′ phase, presenting the intergranular and transgranular mixed.
参考文献
| [1] | 敖三三;罗震;单平;步贤政;刘为东.Inconel601镍基高温合金激光焊焊缝的显微组织[J].中国有色金属学报,2015(8):2099-2107. |
| [2] | 徐向阳;徐滨士;刘文今;刘世参;周仲荣.K417镍基高温合金微动磨损行为的研究[J].航空材料学报,2002(4):13-17. |
| [3] | 赫青山;傅玉灿;陈佳佳;张玮.热管砂轮磨削高温合金GH4169实验研究[J].金刚石与磨料磨具工程,2013(4):5-9. |
| [4] | 乔阳;艾兴;刘战强;赵军.涂层刀具铣削粉末冶金镍基高温合金试验研究[J].华南理工大学学报（自然科学版）,2010(8):83-88. |
| [5] | 任敬心;杨茂奎;李雅卿.镍基高温合金的磨削特征[J].航空学报,1997(06):755. |
| [6] | 苏旭峰.高温合金缓进磨削烧伤机理实验研究[J].中国计量学院学报,2009(01):46-50. |
| [7] | G. W. Goward.Progress in coatings for gas turbine airfoils[J].Surface & Coatings Technology,19981/3(1/3):73-79. |
| [8] | 张健;郭策安;张罡;郝士明.两种NiCrAlY涂层的室温摩擦磨损性能[J].腐蚀科学与防护技术,2011(2):107-110. |
| [9] | 张松;王明生;张开祥;张春华;颜永根.SCH13钢表面激光熔覆CoNiCrAlY合金[J].焊接学报,2010(5):49-52. |
| [10] | 肖旋;郭建亭;于海朋.固溶处理冷却速度对DZ417G合金组织性能的影响[J].材料研究学报,2006(5):533-537. |
| [11] | 张维平;刘文艳.激光熔敷陶瓷涂层综述[J].表面技术,2001(4):30-32,38. |
| [12] | 徐朝政;姜肃猛;马军;宫骏;孙超.两种电弧离子镀Ni-Co-Cr-Al-Si-Y涂层的高温氧化行为[J].金属学报,2009(8):964-970. |
| [13] | 彭新;姜肃猛;段绪海;宫骏;孙超.（MCrAlY+AISiY）复合涂层的高温氧化行为[J].金属学报,2009(3):378-384. |
| [14] | 黄美东;孙超;林国强;董闯;闻立时.脉冲偏压电弧离子低温沉积TiN硬质薄膜的力学性能[J].金属学报,2003(5):516-520. |
| [15] | 何成 .氢对GH690合金拉伸变形行为的影响[D].东北大学,2012. |
| [16] | 李玉芳 .合金元素Zr对Ni<,3>Al力学行为的影响及韧化机制的研究[D].中国科学院金属研究所,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%