通过测量拉伸性能、TEM和SEM分析研究了YB70钢的氢致韧性损伤。结果表明，YB70钢拉伸试样充氢2h以上，其韧性损伤超过80％。在充氢拉伸试样的断口上观察到沿滑移面扩展的穿晶裂纹；基体和碳化物界面处的氢偏聚，使拉伸变形中在距界面约15nm处形成高密度位错缠结，裂纹在位错缠结处形核并沿滑移面扩展，导致了YB70钢的韧性损伤。
Hydrogen induce ductility loss in YBT0 steel was investigated by measurements of tensile properties as well as TEM and SEM analyses of deformation and fracture. The result shows that the hydrogen-induce ductility loss in YBT0 steel exceeds 80 % when tensile specimens were hydrogen-charged for more than 2 h. Some transgranular cracking along slip planes can be observed on the tensile fracture surface of specimens hydrogen-charged. Hydrogen segregation near the interface between the matrix and carbide precipitates promotes the dislocation movement in tensile deformation, leading to a high density of tangled dislocations to be located at approximately 15 nm from the interface. The cracking is formed at the position with the high density of tangled dislocations and propagated along slip planes, which results in the ductility loss of YBT0 steel.
参考文献
| [1] | Reiner Kirchheim .Revisiting hydrogen embrittlement models and hydrogen-induced homogeneous nucleation of dislocations[J].Scripta materialia,2010(2):67-70. |
| [2] | Takahashi Y;Tanaka M;Higashida K et al.An Intrinsic Effect of Hydrogen on Cyclic Slip Deformation Around a {1 1 0} Aatigue Crack in Fe - 3.2 wt.% Si Alloy[J].Acta Materialia,2010,58:1972. |
| [3] | Afrooz Barnoush;Horst Vehoff .Recent developments in the study of hydrogen embrittlement: Hydrogen effect on dislocation nucleation[J].Acta materialia,2010(16):5274-5285. |
| [4] | 张建,李秀艳,赵明久,戎利建.晶界相对Fe-Ni-Cr奥氏体合金氢脆的影响[J].金属学报,2008(09):1095-1098. |
| [5] | 常娥,闫永贵,李庆芬,马力.阴极极化对921A钢海水中氢脆敏感性的影响[J].中国腐蚀与防护学报,2010(01):83-88. |
| [6] | Gao K W;Nakamura M.Microstructures and Hydrogen Embrittlement of Ti-49Al Alloy[J].Intermetallics,2000(08):595. |
| [7] | Hydrogen embrittlement of Cr-Mn-N-austenitic stainless steels[J].International journal of hydrogen energy,2010(3):1485. |
| [8] | Bechtle S;Kumar M;Somerday B P et al.Grain Boundary Engineering Markedly Reduces Susceptibility to Intergranular Hydrogen Embrittlement in Metallic Materials[J].Acta Materialia,2009,57:4148. |
| [9] | Chene J;Noel D;Lecoester F .Hydrogen embrittlement of the Ni-base alloy 600 correlated with hydrogen transport by dislocations[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1/2):173-183. |
| [10] | Zinbi A;Bouehou A .Delayed Cracking in 301 Austenitic Steel After Bending Process,Martensitic Transformation and Hydrogen Embrittlement Analysis[J].Engineering Failure Analysis,2010,17:1028. |
| [11] | Thorsten Michler;Joerg Naumann .Microstructural aspects upon hydrogen environment embrittlement of various bcc steels[J].International journal of hydrogen energy,2010(2):821. |
| [12] | Elhoud A M;Renton N C;Deans W F .Hydrogen Embrittlement of Super Duplex Stainless Steel in Acid Solution[J].International Journal of Hydrogenenergy,2010,35:6455. |
| [13] | Abhay K. Jha;Sushant Manwatkar;K. Sreekumar .Hydrogen-induced intergranular stress corrosion cracking (HI-IGSCC) of 0.35C-3.5Ni-1.5Cr-0.5Mo steel fastener[J].Engineering failure analysis,2010(4):777-786. |
| [14] | Ernesto Villalba;Andrej Atrens .Metallurgical aspects of rock bolt stress corrosion cracking[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):8-18. |
| [15] | Ernesto Villalba;Andrej Atrens .Hydrogen embrittlement and rock bolt stress corrosion cracking[J].Engineering failure analysis,2009(1):164-175. |
| [16] | BIAO Gu;ZHANG Jing wu;WANG Fa-rong et al.The In-Sitn TEM Observation Facilitating Dislocation Enission Multiplication and Motion for Brass[J].Scripta Matllurgica et Materalia,1995,32(04):637. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%