采用超声-电沉积的方法制备了纳米Ni-TiN复合镀层.测试了不同热处理温度下纳米Ni-TiN复合镀层的硬度和磨损量,对镀层的摩擦磨损性能进行了分析.结果表明,热处理温度在300℃时纳米Ni-TiN复合镀层的硬度和耐磨性能最佳,硬度为932.28HV,磨损量为13.5mg;复合镀层的摩擦系数随着热处理温度的升高而略有增大.
参考文献
| [1] | GUO Zhong-cheng;ZHU Cheng-yi;ZHAI Da-cheng-yi .Microstructure of electrodeposited RE-Ni-W-P-SiC composite coating[J].Transactions of Nonferrous Metals Society of China,2000(1):50-52. |
| [2] | Liu L Y;Guo Z C;Xu R D et al.[J].Heat Treatment of Metals,2004,8(29):47-51. |
| [3] | 周月波,张海军.Ni-Al2O3纳米复合镀层的氧化性能研究[J].材料热处理学报,2008(02):154-157. |
| [4] | Nieman G W;Weertman J R;Siegel R W .[J].Materials Research Society,1991,6(05):1012-1027. |
| [5] | Benea L;Bonora P L;Borello A et al.[J].Wear,2001,249(11):995-1003. |
| [6] | N.V.Mandich;J.K.Dennis .Codeposition of Nanodiamonds with Chromium[J].Metal finishing,2001(6):117-119. |
| [7] | 郭鹤桐;张三元.复合镀层技术[M].北京:化学工业出版社,2007 |
| [8] | Low CTJ;Wills RGA;Walsh FC .Electrodeposition of composite coatings containing nanoparticles in a metal deposit[J].Surface & Coatings Technology,2006(1/2):371-383. |
| [9] | 夏法锋 .超声-电沉积镍基TiN纳米复合镀层的研究[D].大连理工大学,2009. |
| [10] | 王天旭,蒙继龙,胡永俊.热处理对铝合金化学镀镍-钨-磷镀层组织性能的影响[J].机械工程材料,2008(01):27-30. |
| [11] | 高诚辉 .[J].摩擦学学报,1997,17(12):302-307. |
| [12] | 张琦,关山,胡如南.热处理温度对硬铬镀层性能的影响[J].北京航空航天大学学报,2002(04):399-401. |
| [13] | 周广宏,丁红燕,章跃.Ni-P-Nano-Al2O3化学复合镀层的磨损机理[J].金属热处理,2004(07):38-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%