以钛酸四丁酯、碳酸钾、硝酸镧、氧氯化锆为原料,采用聚合-络合法制备出了新型的Zr掺杂改性的纳米复合物K2La2Ti3-xZrxO10,通过X射线衍射(XRD)、紫外可见漫反射(DRS)、比表面(BET)以及光致发光(PL)测试对其晶体结构和光学性质进行了表征.以乙醇为电子给体,比较了Zr掺杂量对催化剂光解水活性的影响.结果表明,通过低浓度Zr的掺杂,载Pt后光催化活性得到了大大地提高.Zr掺杂量x=0.2时获得比表面为18.72m2/g的纳米颗粒具有最好的光催化活性,测得其5h内在乙醇溶液中的产氢量子效率为2.69%.
参考文献
| [1] | Fujishima A;Honda K .[J].Nature,1972,238:37-38. |
| [2] | 高濂;郑珊;张青红.纳米氧化钛光催化材料及应用[M].北京:化学工业出版社,2002 |
| [3] | 张莉莉 .硬脂酸法制备超细K2La2Ti3O10及其酸交换性质研究[D].南京:南京理工大学,2003. |
| [4] | Tai Y W;Chen J S;Yang C C et al.[J].Catalysis Today,2004,97:95-101. |
| [5] | Takahashi H;Okubo T;Kakihana M .[J].Chemistry of Materials,1998,10:72-77. |
| [6] | Takata T;Shinohara K;Tanaka A et al.[J].Journal of Photochemistry and Photobiology A:Chemistry,1997,106(03):45-49. |
| [7] | 崔文权,刘利,冯良荣,徐成华,李子健,吕绍洁,邱发礼.Pt/K2La2Ti3O10催化剂的合成及其光催化分解甲醇水溶液制氢[J].中国科学B辑,2006(02):139-144. |
| [8] | Thaminimulla C T K;Takata T;Hara M et al.[J].Journal of Catalysis,2000,196:362-365. |
| [9] | Zhang L L;Zhang W G;Lu L D et al.[J].Materials Science,2006,41:3917-3921. |
| [10] | Shigeru I;Michikazu H;Junko N et al.[J].Chemistry of Materials,1998,10:72-77. |
| [11] | Rabek J F.Experimental Methods in Photochemistry and Photophysics Part 2[M].New York:wiley,1982 |
| [12] | 李涛海,吴季怀,林建明,程应汉.可见光下 H2La2Ti3O10/TiO2光催化降解有机染料的研究[J].环境污染治理技术与设备,2005(04):22-24. |
| [13] | Nozaki R;Kondo J N;Hirose C et al.[J].Journal of Physical Chemistry B,2001,105:7950-7953. |
| [14] | Meng N;Leung M K H;Leung D Y C et al.[J].Renewable & Sustainable Energy Reviews,2007,11(03):401-425. |
| [15] | Kiwi J;Gratzel M .[J].Physical Chemistry,1984,88:1302-1307. |
| [16] | Abe T;Suzuli E;Nagoshi K et al.[J].Journal of Physical Chemistry B,1999,103:1119-1123. |
| [17] | Butler M A .[J].Applied Physics,1977,48:1914-1920. |
| [18] | Yin J;Zou Z G;Ye J H .[J].Journal of Physical Chemistry B,2003,107:4936-4941. |
| [19] | Rahman M M;Krishna K M;Soga T et al.[J].Physical and Chemistry of Solids,1999,60:201-210. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%