通过金属有机源化学气相沉积技术（MOCVD）已可制得Ic达280A／cm，Ic×L为300330A·m的高性能YBCO带材，表现出巨大的优势和诱人的应用前景。进一步提高前驱盐的挥发性和批次稳定性不但能降低YBCO带材的生产成本、也能提高其性能稳定性。本研究报道了MOCVD法制备YBCO所需β-二酮中间体TMHD及其钇、钡、铜金属有机前驱盐的制备，通过红外光谱和核磁共振谱对其化学结构予以确认；同时以金属钡与TMHD在正戊烷或正己烷中制备了无水β-二酮钡盐（Ba[tmhd]2），随后用五乙烯六胺为辅助配体（L）制备了挥发性更好的无水复合配体钡盐（Ba[tmhd]2·L），并通过热重分析技术比较了各前驱盐的挥发性，结果表明：辅助配体五乙烯六胺对提高钡盐挥发性作用显著。
By metal organic chemical vapor deposition process （MOCVD） , the kilometer lengths of YB2Cu3Ox （YB- CO ） second-generation HTS wires with a minimum critical currents of 280A/cm corresponding to a record Ic × length value of 300330 A · mm has been obtained, and MOCVD technique showed great advantage and attractive prospect in YBCO manufacture of high throughput that enables large production capacity. However the conversion efficiency of MOCVD precursor need to be improved for reducing wire cost. In this work, the intermediate 2, 2, 6, 6-tetramethylheptane-3, 5- dionate （tmhd） and corresponding precursors for YBCO, including Y （tmhd） 3, Ba（tmhd） 2 and Cu （tmhd） 2, were synthesized and characterized by infrared spectrum （IR） and 1H nuclear magnetic resonance spectrum （^1H NMR）. Subsequently high volatile Ba（tmhd） 2 （penta） were obtained by using adduct molecule （ penta = pentaethlenehexamine）. Finally their volatility was investigated by thermogravimetry analysis （TGA）.
参考文献
| [1] | Selvamanickam V;Chen Y M;Xiong X M et al.High Perfor manee 2G Wires:From R&D to Pilot-Scale Manufacturing[J].IEEE Transactions on Applied Superconductivity,2009,19(03):3225-3230. |
| [2] | Aytug T;Paranthaman M;Specht E D et al.Enhanced Fux Pinning in MOCVD-YBCO Films through Zr Additions:Systematic Feasibility Studies[J].Superconductor Science and Technology,2010,23:014005. |
| [3] | AMaroni V;Kropf A J;Aytug T et al.Raman and X-Ray Ab-sorption Spectroscopy Characterization of Zr-Doped MOCVD YBa2Cu306+б[J].Superconductor Science and Technology,2010,23:014020. |
| [4] | Selvamanickam, V;Guevara, A;Zhang, Y;Kesgin, I;Xie, Y;Carota, G;Chen, Y;Dackow, J;Zhang, Y;Zuev, Y;Cantoni, C;Goyal, A;Coulter, J;Civale, L .Enhanced and uniform in-field performance in long (Gd, Y)-Ba-Cu-O tapes with zirconium doping fabricated by metal-organic chemical vapor deposition[J].Superconductor Science & Technology,2010(1):014014:1-014014:6. |
| [5] | Selvamanickam V;Kesgin I;Guevara A.Progress in Re- search and Development of IBAD-MOCVD Based Superconducting Wires[M].Washington D C:Applied Superconductivity Confer- ence,2010 |
| [6] | 方继军 .采用光辅助MOCVD方法生长YBCO薄膜和厚度及其特性研究[D].Changchun:.li Lin University,2009. |
| [7] | 李志成,朱延新.2,2,6,6-四甲基-3,5-庚二酮的合成研究[J].化学与生物工程,2007(05):24-26. |
| [8] | Luten H A;Rees Jr W S;Goedken V L .Preparation and Structural Characterization of,and Chemical Vapor Deposition Studies with Certain Yttrium Tris(fl-Diketonate)Compounds[J].Chemical Vapor Deposition,1996,2:149-161. |
| [9] | Hammond G S;Nonthebel D C;Wu C H S.Chelates of fl-Diketonates.V.Preparation and Properties of Chelates Containing Sterically Hindered Ligands[J].Inorganic Chemistry,1963(02):73-76. |
| [10] | Watson I M;Atwood M P;Haq S .Investigations of Barium β- Diketonate Complexes Used in Chemical Vapour Deposition of High-Tc Oxide Films[J].Superconductor Science and Technology,1994,7:627-680. |
| [11] | Turnipseed S B;Barkley R M;Sievers R E .Synthesis and Char- acterization of Alkaline-Earth-Metal β-Diketonate Complexes Used as Precursors for Chemical Vapor Deposition of Thin-Film Super- conductors[J].Inorganic Chemistry,1991,30:1164-1170. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%