利用X射线应力分析仪和在线加载装置测试了紧凑拉伸(compacttension,CT)Be试样缺口前端的应力分布,利用万能拉伸试验机、引伸计和扫描电镜研究了紧凑拉伸Be试样的断裂行为.研究表明:样品加工缺陷如缺口在载荷作用下形成应力集中,样品首先在此开裂,获得了紧凑拉伸铍试样的载荷-裂纹张开曲线和平面应变断裂韧性为15.4MPa√m.扫描电镜观察表明Be断口呈现解理特征,紧凑拉伸试样断口呈现出3个特征区.裂纹尖端扩展观察表明沿基滑移面形成解理微裂纹,这些微裂纹长大后受主应力控制.利用断裂韧性评估了Be材存在微裂纹时的断裂强度.
参考文献
| [1] | Priddy T G .A Consistent Stress-Strain Ductile Fracture Model as Applied to Two Grades of Beryllium,SAND79-2126[R].Livermore:Sandia Laboratories,1979. |
| [2] | Ronald A M .The Use of Notched Beams to Establish Fracture Criteria for Beryllium,UCRL-52866[R].Livermore:Lawrence Livermore Laboratory,1980. |
| [3] | Perra M;Finnie I .Fracture-Toughness Tests on a High-Strength Beryllium from Room Temperature to 3000℃.UCRL-51774[R].Livermore:Lawrence Livermore Laboratory,1975. |
| [4] | Varma R.[A].Nice,France,1997 |
| [5] | Chaouadi R;Scibetta M;Leenaers A .Micromechanical Modeling of Fracture Initiation of Beryllium[R].Belgian:The Belgian Nuclear Research Centre,2005. |
| [6] | GB 4164-1984.GB 4164-1984.金属材料平面应变断裂韧度试验方法[S].Beijing:National Standard Press,1984. |
| [7] | 张鹏程;许彭栓 .热等静压铍的高温拉伸性能研究[R].Mianyang:CAEP Report,1998. |