采用自制的电磁离心铸造机,在磁场强度0.1 T下,对不同转速下电磁离心铸造高碳高速钢的铸态组织和热处理后的组织与性能进行实验研究。结果表明：随着电磁离心铸造机转速的增加,高碳高速钢的铸态组织中共晶碳化物变得越来越细小,沿晶界分布的粗大的碳化物（VC）逐渐变成点状和尖角状。各种转速下,电磁离心铸造高碳高速钢热处理后的硬度、冲击韧度和耐磨性能比普通铸造的高碳高速钢都有明显提高。
Influence of rotational speed of electromagnetic centrifugal casting machine on microstructure and properties of high carbon high speed steel（HC-HSS） was investigated under the condition of the magnetic intensity of 0.1T.The results show that the microstructure of the steel are obviously refined.Meantime,the coarse carbides（VC） along grain boundary is changed into small particles.After heat treatment,hardness,impact toughness and wear resistance of the steel also increase as centrifugal speed increases from 600 r/min to 1370 r/min.
参考文献
| [1] | Hashimoto M;Yoshida K;Otomo S et al.Development of high-toughness roll by CPC process[J].Seitetsu Kenkyu(in Japanese),1990,338:62-66. |
| [2] | 符寒光;邢建东.高速钢轧辊制造技术[M].北京:冶金工业出版社,2007 |
| [3] | 符寒光,邢建东.离心铸造高速钢轧辊铸造缺陷形成与控制技术研究[J].铸造技术,2004(11):859-861. |
| [4] | 张泽磊,杨刚,杨屹.离心铸造研究现状[J].铸造技术,2010(11):1517-1521. |
| [5] | 栾义坤,白云龙,宋男男,康秀红,李殿中.离心铸造轧辊用高速钢的热处理[J].金属学报,2009(04):470-475. |
| [6] | 周宏;王金国;贾树盛 等.不同钒、碳含量高速钢的凝固组织及相组成[J].金属学报,1997,38(08):838-843. |
| [7] | 贾光霖;庞维成.电磁冶金原理与工艺[M].沈阳:东北大学出版社,2003 |
| [8] | 张伟强.金属电磁凝固原理与技术[M].北京:冶金工业出版社,2004 |
| [9] | Jung Ho Lee;Jun cheol Oh;Joon Wook Park .Effects of Tempering Temperature on Wear Resistance and Surface Roughness of a High Speed Steel Roll[J].ISIJ International,2001(8):859-865. |
| [10] | 王钦娟 .电磁离心铸造高速钢轧辊组织及性能研究[D].长安大学,2010. |
| [11] | 王笑天.金属材料学[M].北京:机械工业出版社,1987 |
| [12] | 刘海峰,刘耀辉,于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报,2000(06):401-406. |
| [13] | 徐流杰,魏世忠,张永振,邢建东,龙锐.轧辊用高钒高速钢的滚-滑动磨损性能及失效行为研究[J].摩擦学学报,2009(01):55-60. |
| [14] | 文铁铮;郭玉珍.冶金轧辊技术特性概论[M].石家庄:河北科学技术出版社,1995 |
| [15] | 杜忠泽,符寒光,丰振军,李萍,戴建方.回火处理对铸造高速钢轧辊耐磨性的影响[J].材料热处理学报,2011(02):93-99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%