采用熔融冷淬法制备了Bi2O3.B2O3(30 mol%≤Bi2O3≤60 mol%)二元系统玻璃.运用非等温DSC分析以及S(S)atava和Ozawa-Chen方法研究了Bi2O3-B2O3玻璃的非等温析晶特性,并计算了玻璃的析晶动力学参数.结果表明,在50 mol%≤Bi2O3≤60 mol%范围内,玻璃晶化热处理后可析出针状BiBO3晶体,是原位受控晶化法制备BiBO3晶体的最佳组成范围.添加La2O3和Sm2O3,有助于抑制高聚合度的铋硼酸盐晶体的析出,促进BiBO3晶体的形成;而添加Yb2O3的铋硼酸盐玻璃,晶化热处理后以颗粒状的Bi6810O24晶体为主,不利于BiBO3晶体的析出.对稀土掺杂铋硼酸盐玻璃样品在460～540℃间热处理5 h,可获得表面析晶的透明玻璃样品.
参考文献
| [1] | Heliwig H;Liebertz J;Bohaty L .[J].Solid State Communications,1999,109:249. |
| [2] | Ghotbi M .[J].Applied Physics Letters,2006,89:1. |
| [3] | 滕冰,王继扬,董胜明,胡小波,王正平,邵宗书,刘耀岗.BiB3O6晶体最佳生长方向的确定[J].人工晶体学报,2004(05):751-754. |
| [4] | Wang Z;Xu G;Liu J et al.[J].Journal of the Optical Society of America,2004,B21:1348. |
| [5] | lhara R;Honma T;Fujiwara Y et al.[J].Optical Materials,2004,27:403. |
| [6] | Saisudha M B;Ramakrishna J .[J].Optical Materials,2002,18:403. |
| [7] | Honma T;Bcnino Y;Fujiwara T et al.[J].Optical Materials,2002,20:27. |
| [8] | Ozawa T .[J].Polymer,1971,12(01):150. |
| [9] | (S)atava V .[J].Thermochimica Acta,1971,2(05):423. |
| [10] | Ray C S;Huang W H;Day D E .[J].Journal of the American Ceramic Society,1991,74(01):60. |
| [11] | Marotta A;Saiello S;Buri A .[J].Journal of Non-Crystalline Solids,1983,57(03):473. |
| [12] | Iordanova R;Lefterova E;Uzunov I et al.[J].Journal of Thermal Analysis and Calorimetry,2002,70(02):393. |
| [13] | Yang J H;Dai S H X;Wen L et al.[J].Journal of Applied Physics,2003,93:977. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%