研究了铜基非晶钎料液相的生成和铺展润湿过程.结果表明:非晶钎料由于熔化前固相扩散比较充分,使得钎料中的共晶组织被破坏,生成了大量高熔点的铜固溶体以及铜和镍的化合物,致使非晶钎料产生的液相相对晶态钎料少,因此液相铺展和流动过程较弱.而晶态钎料生成了大量液相,故液相的铺展和流动是晶态钎料钎焊的主过程.由于非晶态钎料非常薄,钎料中原子扩散距离短,有利于快速溶进基材;而普通钎料比较厚,溶解时间较非晶钎料长得多.随钎焊温度的升高和保温时间的延长,钎料残余层的厚度减小.在相同的钎焊温度和保温时间下,非晶态钎料残余层的厚度比晶态钎料小.
参考文献
| [1] | Rabinkin A.[A].San Antonio,Texas:ASM International,2006:148. |
| [2] | De Cristofaro N;Datta A .[J].Rapidly Quenched Metals,1985,1:1715. |
| [3] | De Cristofaro N;Henschel C .[J].Welding Journal,1978,57:33. |
| [4] | Rabinkin A .[J].Issue of Advanced Materials & Processes,2001,7:23. |
| [5] | Shapiro A .[J].Welding Journal,2003,82:36. |
| [6] | Datta A;Rabinkin A;Bose D .[J].Welding Journal,1984,63:14. |
| [7] | Nakahashi M;Shirokane M .[J].Journal of the Japan Institute of Metals,1990,54:826. |
| [8] | Miyazawa Y .[J].Journal of the Japan Welding Society,1992,10:50. |
| [9] | Naka Masaaki;Okamoto Ikuo .[J].Transactions of JWRI(Joining and Welding Research Institute of Osaka University),1985,14:185. |
| [10] | Jyrki M .[J].CALPHAD-Computer Coupling of Phase Diagrams and Thermochemistry,2001,25:67. |
| [11] | 高峰 .铝热交换复合钎料板接头形成机理研究[D].哈尔滨:哈尔滨工业大学,2003. |
| [12] | Yamamura T;Ejima T .[J].Journal of the Japan Institute of Metals,1973,37:901. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%