基金项目: Natural Science Foundation of Liaoning Province (2014020111) National Science Fund for Young Scholars (51405215) High School Development Plan for Distinguished Young Scholars of Liaoning Province Education Committee (LJQ2013067) Project of Higher Education Innovation Team of Liaoning Province (LT2013014) Basic Research Project of Provincial Key Laboratory of Liaoning Education Department (LZ2014031) National High-Tech Research and Development Program of China ("863" Program) (2011AA060102)

关键词：粉末冶金 , Mg-Zn合金 , Zn含量 , 显微组织 , 性能

Effect of Zn on Microstructures and Properties of Mg-Zn Alloys Prepared by Powder Metallurgy Method

Keywords： powder metallurgy method , Mg-Zn alloy , Zn content , microstructure , property

以Mg粉和Zn粉为初始原料,采用粉末冶金技术制备Mg-Zn合金.研究了Zn含量对Mg-Zn合金烧结密度、显微组织、物相组成、弯曲强度和显微硬度的影响.测量了Mg-Zn合金的耐腐蚀性,探讨了Zn元素在粉末冶金过程中的作用机理.结果表明,添加Zn元素后,烧结产物的晶粒细小,烧结密度提高.此外,随着Zn含量的增加,烧结产物的致密度持续增加.XRD分析表明Mg-3％Zn(质量分数)合金主要由α-Mg相组成,而Mg-4％Zn合金由α-Mg和MgZn2两相组成.随着Zn含量的增加,Mg-Zn合金的抗弯曲强度先增加而后降低,但是显微硬度(HV)持续增加.Mg-3％Zn合金的抗弯强度为123.6 MPa,显微硬度为1017 MPa,分别比纯Mg样品高出58％和45％.耐腐蚀性能测试表明当添加Zn元素后,Mg-Zn合金的腐蚀速率降低,Mg-3％Zn合金具有最低的腐蚀速率和最佳的耐腐蚀性能.