以原子比为1:1的Co与Sn金属粉为原料,采用球磨法制备了锂离子电池负极Sn-Co合金,研究了其形成机理及可逆储锂性能.结果表明,球磨先形成CoSn3和CoSn2等中间相,最后形成CoSn2相,继续球磨,CoSn2相的晶粒尺寸先逐渐减小后趋于稳定.晶粒的细化有利于提高合金的首次可逆容量和循环性能,球磨50 h后,首次可逆容量接近最大值,为426 mAh/g,30次循环后容量保持率为67.1%.热处理后,物相转变为CoSn相,提高了合金的循环性能,30次循环后容量保持率为73.7%,但热处理过程中晶粒和颗粒的长大使首次可逆容量降低.
参考文献
| [1] | 沈丁,杨绍斌,张淑凯.锂离子电池锡钴和锡钴碳负极材料的研究进展[J].化工进展,2008(12):1892-1896. |
| [2] | 何见超,赵海雷,贾喜娣,王梦微,陈敬波.锂离子电池Sn-Co合金负极材料的研究进展[J].化工学报,2009(05):1073-1079. |
| [3] | Todd ADW;Mar RE;Dahn JR .Combinatorial study of tin-transition metal alloys as negative electrodes for lithium-ion batteries[J].Journal of the Electrochemical Society,2006(10):A1998-A2005. |
| [4] | Dahn JR;Mar RE;Abouzeid A .Combinatorial study of Sn1-xCox (0 < x < 0.6) and [Sn0.55Co0.45](1-y)C-y (0 < y < 0.5) alloy negative electrode materials for Li-ion batteries[J].Journal of the Electrochemical Society,2006(2):A361-A365. |
| [5] | N. Tamura;M. Fujimoto;M. Kamino;S. Fujitani .Mechanical stability of Sn-Co alloy anodes for lithium secondary batteries[J].Electrochimica Acta,2004(12):1949-1956. |
| [6] | 张敬君,夏永姚.Co-Sn合金作为锂离子电池负极材料的研究[J].高等学校化学学报,2006(10):1923-1926. |
| [7] | 沈丁 .过渡元素对Sn-Co/C基负极材料的结构和电性能的影响[D].阜新:辽宁工程技术大学,2009. |
| [8] | 任榕,吴玉程,汤文明,汪峰涛,郑治祥.退火诱导机械合金化Fe42.5 A142.5 Ti5 B1o合金的结构演变与晶粒生长动力学[J].物理学报,2008(09):5774-5781. |
| [9] | J. Yang;Y. Takeda;N. Imanishi;O. Yamamoto .Ultrafine Sn and SnSb{sub}0.14 powders for lithium storage matrices in lithium-Ion batteries[J].Journal of the Electrochemical Society,1999(11):4009-4013. |
| [10] | 张宁,于维平.电沉积制备锡钴碳复合负极材料的结构与性能[J].材料热处理学报,2008(06):5-8,13. |
| [11] | 杨绍斌,沈丁,李强.Sn_（0.35-0.5x）Co_（0.35-0.5x）Zn_xCo_（0.30）复合材料的制备及电化学性能[J].金属学报,2010(01):6-12. |
| [12] | 王忠,田文怀,李星国.Sn-Sb合金的氢电弧等离子体法制备及其电化学性能[J].物理化学学报,2006(06):752-755. |
| [13] | Zhang JJ;Xia YY .Co-Sn alloys as negative electrode materials for rechargeable lithium batteries[J].Journal of the Electrochemical Society,2006(8):A1466-A1471. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%