对合金Ti-44Al-4Nb-4Hf-1B在700℃大气气氛中开展了长达10 000 h的热暴露处理,系统地探索和分析含Nb-Hf的TiAl合金的高温热稳定性,采用透射电镜和扫描电镜观察合金的显微组织变化并测试相应的力学性能.研究发现:长期大气高温热暴露导致合金中α2+γ层片晶团内的a2层片发生了一定程度的α2→γ相变:部分α2层片转变成为细小的γ层片,到10 000 h时,α2层片的原始厚度减少了约一半.长期大气高温热暴露也导致合金中α2+γ层片条束上发生了α2+γ→B2(ω)相变:条束上部分α2+γ消失,代之以微米及亚微米尺度的B2(ω)块状相.在10 000 h时,其面积分数达到8.4%,随着高温热暴露的逐渐进行,合金的室温塑性伸长率逐渐降低.在10 000h时,合金的塑性约为热暴露前的2/3,表明在复合含Nb+Hf的TiAl合金中,热暴露所导致的“释氧脆化”和“B2+ω生成脆化”的影响有限.复合含Nb+Hf的TiAl合金具有优于单纯含Nb的TiAl合金的高温热稳定性.长期高温热暴露对合金的断裂强度和条件屈服强度没有明显的有害影响.在10 000 h时,其条件屈服强度总体上仍保持在600MPa级别,而合金的室温疲劳极限还有所提高.
参考文献
[1] | 金永元.铌-高温应用[M].北京:冶金工业出版社,2005 |
[2] | 陈国良;林均品.有序金属间化合物结构材料材料物理金属学基础[M].北京:冶金工业出版社,1999 |
[3] | Dimiduk DM .Gamma titanium aluminide alloys--an assessment within the competition of aerospace structural materials[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):281-288. |
[4] | KIM Y W .Ordered intermetallic alloys (part Ⅲ):Gamma titanium aluminides[J].JOM-Journal of the Minerals Metals and Materials Society,1994,46(07):30-39. |
[5] | CHENG T T;WILLIS M R;JONES I P .Effects of major alloying additions on the microstructure and mechanical properties ofγ-TiAl[J].Intermetallics,1999,7:89-99. |
[6] | YOSHINARA M;MIURA K .Ultra-fine equiaxed grain refinement and improvement of mechanical properties of a+βtype titanium alloy by hydrogenation[J].Intermetallics,1995,3:357-363. |
[7] | T.T. Cheng;M.R. Willis .Effect of major alloying additions on the microstructure and mechanical properties of γ-TiAl[J].Intermetallics,1999(1):89-99. |
[8] | HUANG Z W;ZHU D G .Thermal stability of Ti-44Al-8Nb-1B alloy[J].Intermetallics,2008,16:156-167. |
[9] | 史耀君,杜宇雷,陈光.高铌钛铝基合金研究进展[J].稀有金属,2007(06):834-839. |
[10] | 贺跃辉,黄伯云,周科朝,欧文沛,雷长明,陈小群.TiAl基合金显微组织对高温拉伸力学性能的影响[J].中国有色金属学报,1997(01):75-79. |
[11] | HUANG Z W;CONG T .Microstructural instability and embrittlement behaviour of an Al-lean,high-Nb γ-TiAl-based alloy subjected to a long-term thermal exposure in air[J].Intermetallics,2010,18:161-172. |
[12] | HUANG Z W;VOICE W;BOWEN P .Thermal exposure induced α2+γ→B2(ω) and α2→B2(ω) phase transformations in a high Nb lamellar TiAl alloy[J].Scripta Materialia,2003,48:79-84. |
[13] | SILCOCK J M .An X-ray examination of the phase in TiV,TiMo and TiCr alloys[J].Acta Metallurgica,1958,6:481-493. |
[14] | 陈方;黄泽文 .锻压工艺对Ti-44Al-4Nb-4Hf-1B显微组织及拉伸性能的影响[J].西南交通大学学报,2008,43(s):182-185. |
[15] | Shao G.;Tsakiropoulos P. .ON THE #omega# PHASE FORMATION IN Cr-Al AND Ti-Al-Cr ALLOYS[J].Acta materialia,2000(14):3671-3685. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%