利用铜模铸造法制备了(La0.6Ce0.4)65Al10Cu25块体非晶合金,并在其过冷液相区内不同温度下,采用不同压力对该非晶合金进行加压退火处理,通过X射线衍射仪和差示扫描量热法研究了加压退火处理对该非晶合金晶化行为及热稳定性的影响.结果表明,加压退火促进了(La0.6Ce0.4)65Al10Cu25非晶合金的晶化过程,使得晶化初始温度Tx降低(dT/dP=-5.17 K/GPa),晶化激活能EP随退火压力的增加而增大,并从能量和化学短程序畴的角度解释了加压退火对(La0.6Ce0.4)65Al10Cu25非晶合金晶化过程的影响机理.
参考文献
| [1] | Inoue A .[J].Materials Transactions-Japan Institute of Metals,1995,36(05):866. |
| [2] | Peker A;Johnson W L .[J].Applied Physics Letters,1993,68(06):2342. |
| [3] | Yu G S;Lin J G;Ma M et al.[J].Materials Science and Engineering A,2007,460:58. |
| [4] | Jiang JZ.;Rasmussen H.;Kuhn U.;Eckert J.;Lathe C.;Zhou TJ. .Crystallization in Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass under pressure[J].Applied physics letters,2000(22):3553-3555. |
| [5] | Wang ZX.;Zhao DQ.;Pan MX.;Wang WH.;Okada T.;Utsumi W. .Formation and crystallization of CuZrHfTi bulk metallic glass under ambient and high pressures[J].Journal of Physics. Condensed Matter,2003(35):5923-5932. |
| [6] | Li R;Pang S J;Zhang T .[J].Acta Materialia,2007,5(11):3719. |
| [7] | Li R;Pang S J et al.[J].Scripta Materialia,2006,54:1123. |
| [8] | Inoue A;Zhang T .[J].Materials Transactions-Japan Institute of Metals,1989,30(12):965. |
| [9] | Zhang T;Tsai A P;Inoue A et al.[J].Sci Rep Ritu,1992,36(02):261. |
| [10] | 林顺茂 .温挤压Mg基非晶合金及其性能研究[D].北京:北京航空航天大学,2010. |
| [11] | Chen H S .[J].Chemical Physics,1968,48:2560. |
| [12] | 惠希东;陈国良.块体非晶合金[M].北京:化学工业出版社,2007:56. |
| [13] | Chen G L;Hui X D et al.[J].Intermetallics,2002,10:1221. |
| [14] | He D W;Wang W H et al.[J].Journal of Non-Crystallization Solid,2002,297:84. |
| [15] | Kissinger H E .[J].Research of the National Bureau of Standards,1956,57(04):2712. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%