为改善氰酸酯树脂的冲击韧性,在双酚A型二氰酸酯(BADCy)树脂中混入了不同含量的端羧基丁腈橡胶(CTBN).用差示扫描量热法(DSC)及红外光谱法(FTIR)对CTNB/BADCy共混体系的反应性研究发现,CTBN能促进BADCy低温下的三嗪环反应,但是使BADCy的后处理温度提高.SEM分析表明,当CTBN的含量(质量分数)大于15%后,有CTBN颗粒从BADCy中析出,形成两相结构,且随着CTBN含量的增大,分散相的粒径增大,在断口处产生的银纹和剪切带使BADCy/CTBN共混体系的韧性提高.当CTBN的含量为25%时体系的冲击强度提高了2.3倍.
参考文献
| [1] | I.Hamerton, J.N.Hay, Polymer. International., 47(4), 465(1998) |
| [2] | D.Mathew, C.P.R. Nair, K.N.Ninan, Journal of Applied Polymer Science, 74(7), 1675(1999) |
| [3] | G.Loustalot, M.F.Lartigau, P. Grenier, European Polymer Journal, 31(11), 1139(1995) |
| [4] | G.Z.Liang, M.X.Zhang, Journal of Applied Polymer Science, 85, 2377(2002) |
| [5] | J.W.Hwang, S.D.Park, K.Cho, J.K.Kim, C.E.Park, T.S.Oh, Polymer, 38(8), 1835(1997) |
| [6] | Z.Q.Cao, M.Chinf, J.P. Pascault, Ploymer International, 34(1), 41(1994) |
| [7] | J.Borrajo, C.C.Riccardi, R.J.J.Williams, Z.Q.Cao, J.P. Pascault, Ploymer, 36(18), 3541(1995) |
| [8] | WANG Chao, HUANG Yudong, ZHANG Bin, ZHANG Xugang, LI Qili, Polymer Materials Science and Eegineering, 19(3), 145(2003)(王超,黄玉东,张斌,张绪刚,李奇力,高分子材料科学与工程,19(3),145(2003)) |
| [9] | G.Q.Pan, Thermosetting Resin, 17(3), 15(2002)(潘广勤,热固性树脂,17(3),15(2002)) |
| [10] | Y.Feng, Z.P. Fang, A.J.Gu, Polymers for Advanced Technologies, 15, 628(2004) |
| [11] | CHEN Ping, CHENG Zixia, LEI Qingquan, GUO Xinxin, WANG Qingmin, Acta Polymerica Sinica, 4,472(2000)(陈平,程子霞,雷清泉,郭昕昕,王清民,高分子学报,4,472(2000)) |
| [12] | T.Fang, D.A.Shimp, Prog. Polym. Sci., 20, 61(1995) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%