以充分挖掘材料潜力提高中厚板强度级别为目标,开展了普碳钢中厚板的表层组织超细化和心部组织细晶化控轧控冷工艺研究.在形变相变规律研究及实验室轧制工艺摸索的基础上,制定了现场轧制工艺.在首钢中厚板厂3500 mm轧机上,采用化学成分(质量分数,%)为0.13～0.16 C-0.20～0.25 Si-0.80～0.95 Mn-0.01～0.02 P-0.005～0.010 S的连铸坯,成功轧制出表层超细晶中厚钢板.25 mm厚钢板的表层铁索体晶粒度达到12级,中心铁素体晶粒度达到11级,屈服强度达到350～385MPa,抗拉强度达到470～500 MPa,同时保持25%以上的伸长率,完全满足国标GB/T1591-94中规定的Q345 MPa级钢的力学性能要求.本研究对于企业降低冶炼成本,同时提高中厚板产品强韧性具有重要意义.
参考文献
| [1] | Hurley PJ;Muddle BC;Hodgson PD .Analysis and characterisation of ultra-fine ferrite produced during a new steel strip rolling process[J].Scripta materialia,1999(4):433-438. |
| [2] | SUN Zuqing.Study on the Deformation of Undercooled Aus-tenites in Plain Low Carbon Steels[A].上海,2004:68. |
| [3] | SHIN Dong Hyuk.Ultrafine Grained Steels Fabricated by E-qual Channel Angular Pressing[A].海南海口,2005:80. |
| [4] | 翁宇庆.超细晶钢一钢的组织细化理论与控制技术[M].北京:冶金工业出版社,2003:521. |
| [5] | Hidesato Mabuehi .Metallurgical Features of Steel Plates with Uhrafine Grains in Surface Layers and their Formation Mechanism[J].ISIJ International,1999,39(05):477. |
| [6] | 范建文,张维旭,代晓莉,谢瑞萍.普碳钢中板表层组织超细化的变形机理[J].材料热处理学报,2005(06):69-74. |
| [7] | 范建文,谢瑞萍,张维旭,王彦锋,阎智平.表层超细晶粒普碳钢中厚板的工业试制[J].钢铁,2006(04):40-46,55. |
| [8] | Mintz B;姚泽雄;成光祜.微合金化低碳高强度钢[M].北京:冶金工业出版社,1982:51. |
| [9] | V.B.Ginzburg;马东清;陈荣清.板带轧制工艺学[M].北京:冶金工业出版社,1998:50. |
| [10] | 王国栋.400 MPa级超级钢的开发和应用[A].北京:中国铁道出版社,2001:299. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%