高强水泥基材料是水泥基材料的一个重要发展分支.通过介绍高强/高性能混凝土、高致密水泥基均匀体系、无宏观缺陷水泥、活性粉末混凝土等高强水泥基材料的发展、特点、制备方法以及研究应用进展,归纳总结出了水泥基材料高强化的途径,并且指出了高强水泥基材料发展方向与亟待解决的问题.
参考文献
| [1] | ACI Committee 363.State-of-art report on high-strength concrete[J].ACI Journal,1984:364-411. |
| [2] | 屈志中 .国内外超高强混凝土的应用与发展[J].建筑技术,1996,23(01):39-41. |
| [3] | Zia P;Ahmad S;Leming M .High-performance concretes:a state-of-art report[EB/OL].http://www.tfhrc.gov/structur/hpc/hpc2/contnt.htm,2008-10-4. |
| [4] | 蒲心诚.超高强高性能混凝土[M].重庆:重庆大学出版社,2004 |
| [5] | Webb J.High-strength concrete:Economics,design and ductility[J].Concrete International,1993:27-32. |
| [6] | Bache H H.Densified cement/Ultra-fine partiche-based materials[A].Ottawa,Ontario,Canada,1981:10-12. |
| [7] | Bache H H .The new strong cements:their use in structure[J].Physics In Technology,1988,19:43-50. |
| [8] | Lu P;Sun G K;Young J F .Phase composition of hydrated DSP cement paste[J].Journal of the American Chemical Society,1993,76(04):1003-1007. |
| [9] | Lu P;Young J F .Slag-Portland cement based DSP paste[J].Journal of the American Chemical Society,1993,76(05):1329-1331. |
| [10] | 潘国耀,毛若卿,水中和.用超细粉煤灰配制DSP材料的研制[J].武汉工业大学学报,1995(04):4-7. |
| [11] | 柯劲松 .DSP材料的水化特性与高强机理探讨[J].中国建材科技,1996,5(04):21-24. |
| [12] | Hjorth L .Development and application of high-density cement-based materials[J].Philosophical Transactions of the Royal Society of,1983,A310:167-173. |
| [13] | Birchall J D;Howard A J;Kendall K .Flexural strength and porosity of cements[J].Nature,1981,289:388-390. |
| [14] | 柯劲松 .MDF水泥材料的制备与应用[J].中国建材,1995,10:26-27. |
| [15] | 柯劲松;黄从运 .MDF水泥制备工艺条件研究[J].上海建材,1995,5:19-21. |
| [16] | Huang Cong-yun,YUAN Run-zhang,LONG Shi-zong.The Pore Structure and Hydration Performance of Sulphoaluminate MDF Cement[J].武汉理工大学学报(材料科学版)英,2004(01):83-85. |
| [17] | Drabik M;Mojumdar S C;Slade R C T .Prospects of novel maro-defect-free cements for the new millennium[J].Ceramics-Silikaty,2002,46:68-73. |
| [18] | 李北星;张文生 .MDF水泥基复合材料的性能与应用[J].中国建材科技,2000,1:37-41. |
| [19] | 司志明 .MDF水泥复合材料的研究和发展[J].山东建材学院学报,1994,8(04):81-83. |
| [20] | Donatello S;Tyrer M;Cheeseman C R.Recent developments in macro-defect-free(MDF) cements (in press)[J].Construction and Building Materials,2008 |
| [21] | Lee N P;Chrisholm D S .Study report:reactive powder concrete[R].Branz,2006. |
| [22] | 王震宇,陈松来,袁杰.活性粉末混凝土的研究与应用进展[J].混凝土,2003(11):39-41,44. |
| [23] | Richard P;Cheyrezy M .Composition of reactive powder concretes[J].Cement and Concrete Research,1995,25(07):1501-1511. |
| [24] | 何峰,黄政宇.活性粉末混凝土原材料及配合比设计参数的选择[J].新型建筑材料,2007(03):74-77. |
| [25] | Pierre B Y .Precast,prestressed pedestrian bridge-World's first reactive powder concrete structure[J].PCI Journal,1999,9-10:60-71. |
| [26] | Cavill B;Chirgwin G.The world's first RPC road bridge at Shepherds Gully Creed[A].Brisbane,2003 |
| [27] | Ji W Y;An M Z;Yan G P.Study on reactive powder concrete used in the sidewalk system of the Qinghai-Tibet railway bridge[A].北京,2004 |
| [28] | Ming-Gin Lee;Yung-Chih Wang;Chui-Te Chiu .A preliminary study of reactive powder concrete as a new repair material[J].Construction and Building Materials,2007(1):182-189. |
| [29] | Chin-Tsung Liu;Jong-Shin Huang .Highly flowable reactive powder mortar as a repair material[J].Construction and Building Materials,2008(6):1043-1050. |
| [30] | Fernando P T;Joao C G;Said J .Alkali-activated binders:A review.Part 1 Historical background,terminology,reaction mechanisms and hydration products[J].Construction and Building Materials,2008,22:1305-14. |
| [31] | Fernando P T;Joao C G;Said J .Alkali-activated binders:A review.Part 2 About materials and binders manufacture[J].Construction and Building Materials,2008,22:1315-22. |
| [32] | 买淑芳.混凝土聚合物复合材料及其应用[M].北京:科学技术文献出版社,1996 |
| [33] | Steinke R A;Silsbee M R;Agrawal D K et al.Development of chemically bonded ceramics in the CaO-SiO2-P2O5-H2O System[J].Cement and Concrete Research,1991,22:66-72. |
| [34] | Wagh A.Chemically bonded phosphate ceramics:twenty-first century materials with diverse applications[J].Elsevier Sinence,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%