Studies on the Conductivity of Ceramics LaFe1-xNixO3-δ

采用标准的固相反应法制得LaFe1-xNixO3-δ系陶瓷,用双臂电桥原理、四探针法对材料的电阻率进行测试.结果表明,LaFe1-xNixO3-δ系陶瓷在0.6