采用恒载荷拉伸法、腐蚀电化学测试和断口分析技术等，研究了P110钢在不同H2S／CO2含量的NACE-A溶液中的硫化物应力腐蚀（SSCC）行为．结果表明，在加载初期，P110钢的自腐蚀电位Ecorr）急剧下降，至极小值后缓慢升高，达到稳定值后直至断裂，试样断口呈脆性解理状．当通入CO2量达到17％时，P110钢的自腐蚀电位降低，自腐蚀电流（Lcorr）增大，加速钢的SSCC进程，断口形貌为完全解理断裂；随着溶液中通入CO2量增大，钢的自腐蚀电位稍有升高，自腐蚀电流减小，试样断裂时间延长；至CO2量达到50％，断口形貌出现少量韧窝．这种现象的产生与H28／CO2在钢表面的竞争吸附及P110钢在应力腐蚀环境中表面膜的拉伸破裂与再生有关．
Constant load tensile test, electrochemical corrosion measurement and SEM analysis were adopted to study the sulfide stress corrosion cracking （SSCC） of P110 steel in H2S/CO2 NACE standard solution. The results show that, in the initial stage of loading, the Ecorr of P110 steel drops sharply and increases slowly again after reaching a minimum value. Then the Ecorr increases to constant value until fracture occurs, and the brittle cleavage fracture appears correspondingly. When the content of CO2 increasing to 17%, the Ecorr of P110 steel decreases, the corrosion current increases, the process of SSCC is speeding up, and thereby complete cleavage fracture appears correspondingly. With the content of CO2 further increasing, the E,：orr of P110 steel increases slightly, and the corrosion current decreases, the time to fracture is extended. When the content of CO2 increasing to 50%, small quantity of toughness dimples on the fracture surface appears correspondingly. This phenomenon has the relevance to the combination of competitive adsorption of H2S/CO2 on the surface of steel with tensile breakdown and regeneration of surface film on P110 steel in stress corrosion environment.
参考文献
| [1] | 冯星安,黄柏宗,高光第.对四川罗家寨气田高含CO2、H2S腐蚀的分析及防腐设计初探[J].石油工程建设,2004,30(1):10. |
| [2] | 熊有全.川东地区普光气田深井钻井技术[J].当代石油石化,2006,14(8):11. |
| [3] | 张耀丰,丁毅,陆晓峰,304不锈钢在H2S介质条件下的应力腐蚀[J].中国腐蚀与防护学报,2002,27(2):101. |
| [4] | 曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994. |
| [5] | 张学元,柯克,杜元龙.NaCl浓度对APIP105钢在CO2溶液中的电化学腐蚀行为影响[J].中国腐蚀与防护学报,2000,20(5):317. |
| [6] | 陈长风,路民旭,赵国仙.腐蚀产物膜覆盖条件下油套管钢CO2腐蚀电化学特征[J].中国腐蚀与防护学报,2003,23(3):139. |
| [7] | 陈长风,赵国仙,路民旭.N80钢CO2腐蚀产物膜研究[J].中国腐蚀与防护学报,2002,22(3):143. |
| [8] | 李鹤林,白真权,李鹏亮等.模拟CO2/H2S环境中APIN80钢的腐蚀影响因素研究[A].第二届石油石化工业用材研究会论文集[C].成都,2001. |
| [9] | 杨怀玉,陈家坚,曹楚南.H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅲ.不同pH值H2S溶液中碳钢的腐蚀电化学行为[J].中国腐蚀与防护学报,2000,20(2):97. |
| [10] | 阎丽静,林海潮,吴维支.含H2S的强酸性溶液中Cl-对铁腐蚀的影响[J].中国腐蚀与防护学报,1999,19(2):79. |
| [11] | 魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1996. |
| [12] | 李春福,邓洪达,王斌.高含H2S/CO2环境中套管钢腐蚀行为与腐蚀产物膜关系[J].材料热处理学报,2008,29(1):90. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%