纳米金红石型二氧化钛是一种重要的新型无机功能材料，其制备及其应用在当代愈来愈受到重视．本文利用ZnCO3包覆Ti（OH）4沉淀，500℃预焙解，使ZnCO3转变为ZnO；Ti（OH）4转变为H2TiO3．然后溶去97wt％的包覆ZnO粉体，800℃焙烧，最终制得粒径约20～60nm的金红石型二氧化钛粉体．利用TEM、XRD、ICP对粉体粒子的形貌、大小、物相及化学组成进行了分析．
Nanometer rutile TiO2 is a new kind of inorganic functional material. its preparation and application have been paid more and more attention.
In this study, ZnCO3 was used to coat on the surface of Ti(OH)4, then heating to make ZnCO3 transfer to ZnO and Ti(OH)4 transfer to H2TiO3
at 500℃, dissolving about 97wt% coated ZnO powder. Finally ,the rutile TiO2 powders were prepared after having calcined the H2TiO3 powder
(containing 3wt%ZnO) at 800℃, and the particle size was about 20～60nm obtained. The morphology, size, composition of rutile TiO2 powders were studied by
means of TEM, ICP and XRD.
参考文献
| [1] | 李学富. 化工新型材料, 1995, (5): 36--39. [2] 乐志强. 化工进展, 1991, (8): 47--51. [3] Yoko Suyama, Akio Kato. J. Amer. ceram. Soc., 1976, 59 (3): 146--149. [4] Akhtar M K, Vemury S, et al. Nanostructure Materials 1994, 4 (5): 537--544. [5] Kamal M, et al. J. Amer. Ceram. Soc., 1992, 75 (12): 3408--3410. [6] Terabe K, Kato K, et al. J. Mater. Sci., 1994, 29: 1617--1622. [7] 于网林, 杨平, 陈宗淇. 高等学校化学学报 1994, 15 (11): 1686--1689. [8] 孙康, 王永刚. 无机盐工业, 1997, (3): 9--10. [9] 陈代荣, 孟祥建 (CHEN Dai-Rong, et al). 无机材料学报(Journal of Inorganic Materials), 1997, 12 (1): 110--114. [10] Dulin F H, Rase D E. J. America Ceramic of Society, 1960, 43 (3): 125--131. [11] 丁星兆, 罗利(DING Xing-Zhao, et al). 无机材料学报 (Journal of Inorganic Materials), 1993, 8 (1): 115--117. |