为改善常规凝固条件下镁合金微观组织粗大,力学性能较差等缺点,用单辊快速凝固法制备了Mg_(52)Zn_(35)Nd_(13)合金急冷薄带.采用透射电镜、X射线衍射仪、热分析仪等手段研究了急冷态及退火态薄带的显微组织、相结构转变与性能特点.实验结果表明:急冷薄带显微组织中存在大量非晶态结构.退火处理发现,在本实验条件下,102℃×3 h退火条件下薄带显微组织结构最佳,力学性能最好.而后薄带微观组织将随退火温度的不断升高而明显粗化,力学性能不断下降.该合金成分具有一定的非晶成形能力;快速凝固工艺可显著改善镁合金微观组织粗大等缺陷;适当的退火工艺可进一步优化急冷薄带微观组织并获得更好力学性能.
To improve the coarse microstructure and mechanical properties of magnesium alloy under conditions of conventional solidification,single-roll rapid solidification ribbon of Mg_(52)Zn_(35)Nd_(13) alloys was prepared by quenching.The microstructure,phase structure transformation and performance characteristics of quenching state and annealed ribbons were studied by means of transmission electron microscopy,X-ray diffraction,and thermal analysis instrument.Experimental results show that a large number of amorphous structures exist in quench microstructure of thin strip.The best thin strip microstructure and mechanical properties can be obtained through annealing for 3 h at 102℃.Then the microstructure of thin strip turns to be coarse with rising annealing temperature,and its mechanical properties are weakened.The alloy composition has a certain capability of amorphous forming.Rapid solidification process can significantly improve the coarse microstructure of magnesium alloy.Appropriate annealing process can further optimize the quenching microstructure of thin strip and achieve better mechanical properties.
参考文献
| [1] | 夏德宏,郭梁,余涛.镁与镁合金广阔的应用前景[J].金属世界,2005(02):47-48. |
| [2] | Y.L REN;J.H. ZUO;K.Q. QIU .Eutectic structure and bulk glass formation in Mg-based alloys[J].Intermetallics,2004(10/11):1205-1209. |
| [3] | X.K. Xi;D.Q. Zhao;M.X. Pan .On the criteria of bulk metallic glass formation in MgCu-based alloys[J].Intermetallics,2005(6):638-641. |
| [4] | Makoto Matsuura;Masaki Sakurai;Kenji Amiya .Local structures around Zn and Y in the melt-quenched Mg_(97)Zn_1Y_2 ribbon[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):240-245. |
| [5] | 陈吉华,陈振华,严红革.快速凝固镁合金的研究进展[J].化工进展,2004(08):816-822. |
| [6] | P.M. Jardim;G. Solorzano;J.B. Vander Sande .Second phase formation in melt-spun Mg-Ca-Zn alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):196-205. |
| [7] | Maeng D.Y.;Kim T.S. .MICROSTRUCTURE AND STRENGTH OF RAPIDLY SOLIDIFIED AND EXTRUDED Mg-Zn ALLOYS[J].Scripta materialia,2000(5):358-389. |
| [8] | Y.-K. Xu;H. Ma;J. Xu .Mg-based bulk metallic glass composites with plasticity and gigapascal strength[J].Acta materialia,2005(6):1857-1866. |
| [9] | Michiaki Yamasaki;Naoyuki Hayashi;Shogo Izumi;Yoshihito Kawamura .Corrosion behavior of rapidly solidified Mg-Zn-rare earth element alloys in NaCl solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(1):255-262. |
| [10] | Yeon-Wook Kim .Microstructures and Mechanical Properties of Rapidly Solidified Mg-Al-Zn-MM Alloys[J].Journal of materials science & technology,2008(1):89-92. |
| [11] | 黄正华,郭学锋,张忠明.快速凝固AZ91D镁合金组织的研究[J].材料热处理学报,2005(01):32-35. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%