在温度高达2023K,可控氧分压和不同应变速率条件下,对钇铝榴石单晶体进行了蠕变实验.研究表明、钇铝榴石晶体的脆-延性转变温度高达1833K.在温度低于2023K和应变速率大于10-5·s-1的条件下,其蠕变流动强度高于300MPa.对钇铝榴石晶体蠕变机制的研究表明,其高温塑性变形起因于晶体的位错滑移,晶体在高温下的高强度与其很高的Peierls力相关.钇铝榴石晶体在高温下的晶体稳定性和超高强度使其有可能替代金刚石,在高温高压和特殊的化学环境下应用.
The strength and rheology of YAG Single crystal garnet at the conditions of T=1673~1973K, ε = 10-7~10-5s-1 and fo2 = 10 fpa~ 10 kPa were studied. The results show that brittle-ductile transiton of YAG crystal occurs at fairly high temperature (>1873K) whe
参考文献
| [1] | KaratoS．PhysEarthPlanetInter,1989,55:2342CormanGS．USAirForce,F33615-87-C-5545,1990:883KaratoS．WangZC,FlljinoKEarthPlanetSciLett,1995,130:304RabierJ,GaremHIn:TresslerRE,BradtRCeds．DeformationofCeramicMaterials．NewYork,1984:1875ParthaserathyTA,MahTI,MatsonLE．AmerCeramSoc,1993,76:296KaratoS,WangZC,FujinoKJMaterialsSci,1994,7WangZC,KaratoS,FuJinoKPhysEarthPlanetInter,1993,79:2998KurishitaK．In:ProceedingofInternationalConferenceonHighPressureandHighTemperatue,Warsaw,Poland,1995,2 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%