采用恒载荷缺口拉伸试验和慢应变速率拉伸试验研究了30CrMnSiA钢在不同回火温度下的氢致延迟断裂行为.结果表明,随着回火温度的提高,实验钢的延迟断裂抗力逐渐提高,510℃回火时可获得良好的耐延迟断裂性能.实验钢在充氢前的断裂机制为准解理+少量韧窝断裂,且随着回火温度的升高,断口中韧窝断裂的比例增加;实验钢在充氢后或在腐蚀液中加载时,350℃和400℃回火试样的断裂机制转变为氢致沿晶断裂,510℃回火试样的断裂机制则未发生变化.
参考文献
| [1] | 李光福,吴忍畊,雷廷权 .回火温度对42CrMo高强钢应力腐蚀断裂行为的影响[J].中国腐蚀与防护学报,1991,11(1):27-33 LI Guang-fu,W U Ren-geng,LEI Ting-quan.Effect of tempering temperature on stress corrosion cracking behavior of 42CrMo high strength steel[J].Journal of Chinese Society for Corrosion and Protection,1991,11 (1):27-33.,1991. |
| [2] | Nakatani Y,Higashi T,Yamada K .Effect of tempering treatment on hydrogen-induced cracking in high-strength steel[J].Fatigue Fact Engng Mater Struct,1999,22 |
| [3] | 武光宗,王毛球,王春芳,甘国友,董瀚.回火马氏体钢中氢的扩散行为及其氢脆敏感性[J].材料热处理学报,2012(01):136-140. |
| [4] | Kim J S,Lee Y H .Microstructural influences on hydrogen delayed fracture of high strength steels[J].Material Science and Engineering A,2009,505 |
| [5] | 惠卫军,翁宇庆,董瀚.高强度紧固件用钢[M].北京:冶金工业出版社,2009.,2009. |
| [6] | 刘昌奎,臧金鑫,张兵.30CrMnSiA螺栓断裂原因分析[J].失效分析与预防,2008(02):42-47. |
| [7] | 王玉玲,王俊.30CrMnSiA螺栓失效分析[J].机械工程材料,2008(05):71-73. |
| [8] | 李仁顺,吴忍畊,黄小兵,等.高强度螺栓用30CrMnSiA钢的工艺氢脆[J].航天工艺,1983(10):30-40.LI Ren-shun,WU Ren-geng,HUANG Xiao-bing,et al.Hydrogen embrittlement of 30CrMnSiA bolt with high strength[J].Aerospace Manufacturing Technology,1983 (10):30-40.,1983. |
| [9] | Li G F,Wu R G,Lei T C .Carbide-matrix interface mechanism of stress corrosion cracking behavior of high-strength Cr-Mo steels[J].Metallurgical Transactions A,1992,23(10):2879-2885.,1992. |
| [10] | 李光福,吴忍畊,雷廷权,等低合金超高强度钢的晶界性质对应力腐蚀断裂行为的影响[J].宇航学报,1996,16(3):58-63.LI Guang-fu,WU Ren-geng,LEI Ting-quan,et al.Effect of grain boundary properties on the stress corrosion cracking behavior of ultrahigh strength low alloy steel[J].Journal of Astronautics,1996,16 (3):58-63.,1996. |
| [11] | 王继尧,晁月盛,赵秉军,等 .30CrMnSiA钢的回火组织转变[J].材料科学与工艺,1994,2(4):33-38.WANG Ji-yao,CHAO Yue-sheng,ZHAO Bing-jun,et al.Microstructure transformation of 30CrMnSiA steel under tempering condition[J].Material Science and Technology,1994,2 (4):33-38.,1994. |
| [12] | 惠卫军,董瀚,翁宇庆,王毛球,时捷.Cr-Mo-V系高强度钢的应力腐蚀开裂行为[J].材料热处理学报,2006(06):37-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%